Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC ML-3500ZBL TEIJIN SHANGHAI
PANLITE®
Casters、Electrical applications、Lighting applications、light-emitting diode、Lighting diffuser
Light diffusion、Flame retardant、Weather resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TEIJIN SHANGHAI/ML-3500ZBL |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179 | NoBreak |
| Mechanical properties | Test Condition | Test Method | TEIJIN SHANGHAI/ML-3500ZBL |
|---|---|---|---|
| Tensile stress | 断裂 | ISO527-2/50 | 54.0 Mpa |
| 屈服 | ISO527-2/50 | 61.0 Mpa | |
| Tensile modulus | ISO527-2/1 | 2400 Mpa | |
| Bending modulus 2 | ISO178 | 2100 Mpa | |
| Bending stress 2 | ISO178 | 93.0 Mpa | |
| Tensile strain | 屈服 | ISO527-2/50 | 6.0 % |
| Nominal tensile fracture strain | ISO527-2/50 | >50 % |
| Electrical performance | Test Condition | Test Method | TEIJIN SHANGHAI/ML-3500ZBL |
|---|---|---|---|
| Surface Resistivity | IEC60093 | >1.0E+15 ohms | |
| Volume resistivity | IEC60093 | >1.0E+15 ohms·cm |
| optical performance | Test Condition | Test Method | TEIJIN SHANGHAI/ML-3500ZBL |
|---|---|---|---|
| transmissivity | 3000µm | ASTMD1003 | 52.0 % |
| flammability | Test Condition | Test Method | TEIJIN SHANGHAI/ML-3500ZBL |
|---|---|---|---|
| Hot filament ignition temperature | 3.0mm | IEC60695-2-13 | 875 °C |
| UL flame retardant rating | 3.0mm | UL94 | V-2 |
| Burning wire flammability index | 1.5mm | IEC60695-2-12 | 850 °C |
| Hot filament ignition temperature | 1.5mm | IEC60695-2-13 | 875 °C |
| UL flame retardant rating | 1.5mm | UL94 | V-2 |
| Burning wire flammability index | 3.0mm | IEC60695-2-12 | 960 °C |
| UL flame retardant rating | 0.40mm | UL94 | V-2 |
| physical property | Test Condition | Test Method | TEIJIN SHANGHAI/ML-3500ZBL |
|---|---|---|---|
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 8.00 cm3/10min |
| Water absorption rate | 23°C,24hr | ISO62 | 0.20 % |
| Shrinkage rate | MD:4.00mm | 内部方法 | 0.50to0.70 % |
| TD:4.00mm | 内部方法 | 0.50to0.70 % |
| Thermal performance | Test Condition | Test Method | TEIJIN SHANGHAI/ML-3500ZBL |
|---|---|---|---|
| TD | ISO11359-2 | 7E-05 cm/cm/°C | |
| RTI Elec | 1.5mm | UL746 | 125 °C |
| RTI Str | 1.5mm | UL746 | 125 °C |
| 1.8MPa,未退火 | ISO75-2/A | 129 °C | |
| RTI Imp | 1.5mm | UL746 | 115 °C |
| MD | ISO11359-2 | 7E-05 cm/cm/°C |