PLA+PC ECO PELLET® LC52A UMG JAPAN
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | UMG JAPAN/ECO PELLET® LC52A |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 12 kJ/m² |
| hardness | Test Condition | Test Method | UMG JAPAN/ECO PELLET® LC52A |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | ISO 2039-2 | 115 |
| Mechanical properties | Test Condition | Test Method | UMG JAPAN/ECO PELLET® LC52A |
|---|---|---|---|
| Flexural modulus | 23°C | ISO 178 | 3000 MPa |
| tensile strength | 23°C | ISO 527-2 | 58.0 MPa |
| bending strength | 23°C | ISO 178 | 90.0 MPa |
| flammability | Test Condition | Test Method | UMG JAPAN/ECO PELLET® LC52A |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | UMG JAPAN/ECO PELLET® LC52A |
|---|---|---|---|
| Shrinkage rate | MD：23°C | ISO 294-4 | 0.50to0.80 % |
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 29.0 cm³/10min |
| density | 23°C | ISO 1183 | 1.22 g/cm³ |
| Thermal performance | Test Condition | Test Method | UMG JAPAN/ECO PELLET® LC52A |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/Af | 92.0 °C |