PC LUX2114-WH5G007X SABIC INNOVATIVE NANSHA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/LUX2114-WH5G007X |
---|---|---|---|
-30°C | ISO 180/1U | 无断裂 | |
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 65 kJ/m² |
23°C | ISO 180/1A | 65 kJ/m² | |
Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
23°C | ISO 179/1eU | 无断裂 | |
23°C | ASTM D256 | 600 J/m | |
ISO 180/1U | 无断裂 | ||
Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 12 kJ/m² |
-30°C | ISO 180/1A | 11 kJ/m² | |
23°C | ASTM D4812 | 3200 J/m | |
Impact strength of cantilever beam gap | ASTM D1822 | 546 kJ/m² | |
Dart impact | 23°C | ASTM D3029 | 169 J |
hardness | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/LUX2114-WH5G007X |
---|---|---|---|
Rockwell hardness | M级 | ASTM D785 | 70 |
R级 | ASTM D785 | 118 |
Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/LUX2114-WH5G007X |
---|---|---|---|
Dissipation Factor | 50Hz | ASTM D150 | 9E-04 |
60Hz | ASTM D150 | 9E-04 | |
dielectric constant | 60Hz | ASTM D150 | 3.17 |
Volume resistivity | ASTM D257 | >1.0E+17 ohms·cm | |
dielectric constant | 50Hz | ASTM D150 | 3.17 |
Dissipation Factor | 1MHz | ASTM D150 | 0.010 |
High arc combustion index (HAI) | HAI | UL 746 | PLC 1 |
Hot wire ignition (HWI) | HWI | UL 746 | PLC 3 |
dielectric constant | 1MHz | ASTM D150 | 2.96 |
dielectric strength | 3.20mm,inAir | ASTM D149 | 15 KV/mm |
Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 3 |
Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/LUX2114-WH5G007X |
---|---|---|---|
elongation | 断裂 | ASTM D638 | 110 % |
bending strength | 屈服,50.0mm跨距 | ASTM D790 | 93.1 Mpa |
elongation | 屈服 | ASTM D638 | 7.0 % |
tensile strength | 断裂 | ASTM D638 | 65.5 Mpa |
Taber abraser | 1000Cycles,1000g,CS-17转轮 | ASTM D1044 | 10.0 mg |
tensile strength | 屈服 | ASTM D638 | 62.1 Mpa |
Flexural modulus | 50.0mm跨距 | ASTM D790 | 2340 Mpa |
flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/LUX2114-WH5G007X |
---|---|---|---|
Hot filament ignition temperature | 1.50mm | IEC 60695-2-13 | 850 °C |
Burning wire flammability index | 0.750mm | IEC 60695-2-12 | 750 °C |
Hot filament ignition temperature | 0.750mm13 | IEC 60695-2-13 | 875 °C |
Burning wire flammability index | 1.50mm | IEC 60695-2-12 | 850 °C |
UL flame retardant rating | 0.750165mm | UL 94 | V-2 |
physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/LUX2114-WH5G007X |
---|---|---|---|
Shrinkage rate | MD:3.20mm | 内部方法 | 0.50-0.70 % |
Water absorption rate | 24hr | ASTM D570 | 0.15 % |
Outdoor applicability | UL 746C | f2 | |
Water absorption rate | 平衡,23°C | ASTM D570 | 0.35 % |
Specific volume | ASTM D792 | 0.830 cm³/g | |
Water absorption rate | 平衡,100°C | ASTM D570 | 0.58 % |
melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 18 g/10min |
Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/LUX2114-WH5G007X |
---|---|---|---|
Heat distortion temperature | 1.8MPa,未退火,6.40mm,HDT | ASTM D648 | 132 °C |
vicat | ASTM D152512 | 154 °C | |
thermal conductivity | ASTMC177 | 0.25 W/m/K | |
Linear coefficient of thermal expansion | MD:-40到95°C | ASTME831 | 6.8E-05 cm/cm/°C |
Heat distortion temperature | 0.45MPa,未退火,6.40mm,HDT | ASTM D648 | 138 °C |
RTI Imp | UL 746 | 80.0 °C | |
RTI | UL 746 | 80.0 °C | |
specific heat | ASTMC351 | 1260 J/kg/°C | |
ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
RTI Elec | UL 746 | 80.0 °C |