PC EXL1132T-GY2G293 SABIC INNOVATIVE NANSHA
LEXAN™
Household appliances、Automotive sector、Electronic field、Electrical field
Low temperature resistanc、Easy to process、High mobility、UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL1132T-GY2G293 |
|---|---|---|---|
| RTI | UL 746 | 130 °C | |
| Ball PressureTest | 123 到 127°C | IEC 60695-10-2 | 通过 |
| Linear thermal expansion coefficient | 流动 : 23 到 80°C | ISO 11359-2 | 7.5E-5 cm/cm/°C |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 9 | ISO 75-2/Af | 116 °C |
| Vicat Softening Temperature | -- | ISO 306/B120 | 139 °C |
| Linear thermal expansion coefficient | 横向 : -40 到 95°C | ASTM E831 | 7.6E-5 cm/cm/°C |
| RTI Elec | UL 746 | 130 °C | |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 121 °C |
| Vicat Softening Temperature | -- | ASTM D152510, ISO 306/B5010 | 138 °C |
| Linear thermal expansion coefficient | 流动 : -40 到 95°C | ASTM E831 | 7.5E-5 cm/cm/°C |
| 横向 : 23 到 80°C | ISO 11359-2 | 7.6E-5 cm/cm/°C |
| Hardness | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL1132T-GY2G293 |
|---|---|---|---|
| Rockwell Hardness | L 计秤 | ISO 2039-2 | 89 |
| Injection | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL1132T-GY2G293 |
|---|---|---|---|
| Middle Temperature | 280 到 305 °C | ||
| Drying Time | 3.0 到 4.0 hr | ||
| Suggested Shot Size | 40 到 60 % | ||
| Drying Temperature | 120 °C | ||
| Mold Temperature | 70 到 95 °C | ||
| Vent Depth | 0.025 到 0.076 mm | ||
| Suggested Max Moisture | 0.020 % | ||
| Processing (Melt) Temp | 295 到 315 °C | ||
| Rear Temperature | 270 到 295 °C | ||
| Nozzle Temperature | 290 到 310 °C | ||
| Front Temperature | 295 到 315 °C | ||
| Back Pressure | 0.300 到 0.700 Mpa | ||
| Screw Speed | 40 到 70 rpm |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL1132T-GY2G293 |
|---|---|---|---|
| Moisture Absorption | 平衡, 23°C, 50% RH | ISO 62 | 0.090 % |
| Melt Mass-Flow Rate | 300°C/1.2 kg | ASTM D1238 | 20 g/10 min |
| Modeling Shrinkage | 横向流动 : 3.20 mm | 内部方法 | 0.40 到 0.80 % |
| 流动 : 3.20 mm | 0.40 到 0.80 % | ||
| Moisture Absorption | 饱和, 23°C | ISO 62 | 0.12 % |
| Melt Volume flow Rate | 300°C/1.2 kg | ISO 1133 | 19.0 cm3/10min |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL1132T-GY2G293 |
|---|---|---|---|
| Tensile Strength | 断裂 | ISO 527-2/50 | 56.0 Mpa |
| Tensile Modulus | -- | ISO 527-2/1 | 2340 Mpa |
| Tensile Elongation | 断裂 3 | ASTM D638 | 120 % |
| Tensile Strength | 屈服 3 | 58.0 Mpa | |
| Tensile Elongation | 屈服 | ISO 527-2/50 | 5.4 % |
| Flexural Modulus | 50.0 mm 跨距 4 | ASTM D790 | 2240 Mpa |
| Tensile Modulus | -- 2 | ASTM D638 | 2260 Mpa |
| Tensile Strength | 屈服 | ISO 527-2/50 | 57.0 Mpa |
| Flexural Stress | 屈服, 50.0 mm 跨距 4 | ASTM D790 | 94.0 Mpa |
| Tensile Elongation | 屈服 3 | ASTM D638 | 5.7 % |
| Flexural Stress | -- 5, 6 | ISO 178 | 89.0 Mpa |
| Flexural Modulus | -- 5 | 2140 Mpa | |
| Tensile Elongation | 断裂 | ISO 527-2/50 | 120 % |
| Tensile Strength | 断裂 3 | ASTM D638 | 57.0 Mpa |
| Optical | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL1132T-GY2G293 |
|---|---|---|---|
| Haze | 2540 µm | ASTM D1003 | 3.0 % |
| Transmittance | 82.0 % |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL1132T-GY2G293 |
|---|---|---|---|
| Unnotched Izod Impact Strength | 23°C | ISO 180/1U | 无断裂 |
| Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 74.0 J |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 45 kJ/m² |
| 23°C | 65 kJ/m² | ||
| Charpy Unnotched Impact Strength | ISO 179/1eU | 无断裂 | |
| Unnotched Izod Impact Strength | -30°C | ISO 180/1U | 无断裂 |
| Charpy Unnotched Impact Strength | ISO 179/1eU | 无断裂 |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL1132T-GY2G293 |
|---|---|---|---|
| Glow Wire Flammability Index | 3.0 mm | IEC 60695-2-12 | 960 °C |
| Glow Wire Ignition Temperature | 0.8 mm | IEC 60695-2-13 | 850 °C |
| 3.0 mm | 850 °C | ||
| UL flame retardant rating | 1.5 mm | UL 94 | HB |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL1132T-GY2G293 |
|---|---|---|---|
| Volume Resistivity | ASTM D257 | > 1.0E+15 ohms·cm | |
| Surface Resistivity | > 1.0E+15 ohms |