Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS LARTON G/40 LATI ITALY
--
--
Filler: Glass fiber reinf、40% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LATI ITALY/LARTON G/40 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -20°C | ISO179/1eU | 28 kJ/m² |
| 23°C | ISO179/1eU | 30 kJ/m² |
| Mechanical properties | Test Condition | Test Method | LATI ITALY/LARTON G/40 |
|---|---|---|---|
| Tensile strain | 断裂,60°C | ISO527-2/5 | 1.7 % |
| Tensile stress | 断裂,150°C | ISO527-2/5 | 75.0 Mpa |
| 断裂,120°C | ISO527-2/5 | 100 Mpa | |
| Tensile strain | 断裂,120°C | ISO527-2/5 | 3.0 % |
| 断裂,150°C | ISO527-2/5 | 3.4 % | |
| Tensile stress | 断裂,60°C | ISO527-2/5 | 170 Mpa |
| Tensile strain | 断裂,90°C | ISO527-2/5 | 2.0 % |
| Tensile stress | 断裂,23°C | ISO527-2/5 | 185 Mpa |
| Tensile modulus | 23°C | ISO527-2/1 | 16000 Mpa |
| 60°C | ISO527-2/1 | 15500 Mpa | |
| 90°C | ISO527-2/1 | 15000 Mpa | |
| 120°C | ISO527-2/1 | 9800 Mpa | |
| 150°C | ISO527-2/1 | 6800 Mpa | |
| Tensile stress | 断裂,90°C | ISO527-2/5 | 140 Mpa |
| Tensile strain | 断裂,23°C | ISO527-2/5 | 1.4 % |
| Electrical performance | Test Condition | Test Method | LATI ITALY/LARTON G/40 |
|---|---|---|---|
| 解决方案A | IEC60112 | 125 V |
| flammability | Test Condition | Test Method | LATI ITALY/LARTON G/40 |
|---|---|---|---|
| Burning wire flammability index | 2.0mm | IEC60695-2-12 | 960 °C |
| Limiting Oxygen Index | ASTMD2863 | 44 % | |
| Burning wire flammability index | 1.0mm | IEC60695-2-12 | 960 °C |
| UL flame retardant rating | 3.0mm | UL94 | V-0 |
| 0.75mm | UL94 | V-0 | |
| 1.5mm | UL94 | V-0 |
| physical property | Test Condition | Test Method | LATI ITALY/LARTON G/40 |
|---|---|---|---|
| Shrinkage rate | MD:2.00mm | ISO294-4 | 0.20到0.35 % |
| TD:2.00mm | ISO294-4 | 0.45到0.65 % | |
| Water absorption rate | 23°C,24hr | ISO62 | 0.040 % |
| Thermal performance | Test Condition | Test Method | LATI ITALY/LARTON G/40 |
|---|---|---|---|
| 连续使用温度4 | 220 °C | ||
| MD：30到100°C | ISO11359-2 | 6E-06 cm/cm/°C | |
| 0.45MPa,未退火 | ISO75-2/B | 280 °C | |
| vicat | ISO306/B50 | 255 °C | |
| 1.8MPa,未退火 | ISO75-2/A | 270 °C |