PA12 3030LUX UBE JAPAN
--
Pipe fittings
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | UBE JAPAN/3030LUX |
|---|---|---|---|
| Shore hardness | 邵氏D | ISO 868 | 78 |
| Rockwell hardness | R计秤 | ISO 2039-2 | 105 |
| Mechanical properties | Test Condition | Test Method | UBE JAPAN/3030LUX |
|---|---|---|---|
| bending strength | ISO 178 | 60.0 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 200 % |
| Flexural modulus | ISO 178 | 1500 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 5.0 % |
| tensile strength | 屈服 | ISO 527-2 | 47.0 Mpa |
| Electrical performance | Test Condition | Test Method | UBE JAPAN/3030LUX |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+15 ohms·cm |
| physical property | Test Condition | Test Method | UBE JAPAN/3030LUX |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 1.5 % |
| MD | ISO 294-4 | 0.60 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.60 % |
| melt mass-flow rate | 235°C/2.16kg | ISO 1133 | 3.0 g/10min |
| Thermal performance | Test Condition | Test Method | UBE JAPAN/3030LUX |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 112 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 49.0 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.2E-04 cm/cm/°C |
| melting temperature | ISO 3146 | 178 °C |