Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 505R SABIC INNOVATIVE US
LEXAN™
Lighting applications,Plastic bag
Middle flow,Thermal stability
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/505R |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C8 | ISO 179/1eU | NoBreak |
| -30°C9 | ISO 179/1eU | NoBreak | |
| -30°C8 | ISO 179/1eU | NoBreak | |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 110 J/m |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 61.0 J |
| Impact strength of simply supported beam without notch | 23°C9 | ISO 179/1eU | NoBreak |
| Suspended wall beam without notch impact strength | 23°C10 | ISO 180/1U | NoBreak |
| Impact strength of cantilever beam gap | -30°C10 | ISO 180/1A | 8.0 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/2C | 15 kJ/m² |
| Impact strength of cantilever beam gap | -30°C11 | ISO 180/1A | 8.0 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C11 | ISO 180/1U | NoBreak |
| -30°C10 | ISO 180/1U | NoBreak | |
| Charpy Notched Impact Strength | -30°C8 | ISO 179/1eA | 9.0 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 80 J/m |
| Charpy Notched Impact Strength | 23°C9 | ISO 179/1eA | 9.0 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ASTM D4812 | 1600 J/m |
| Suspended wall beam without notch impact strength | -30°C11 | ISO 180/1U | 130 kJ/m² |
| Charpy Notched Impact Strength | 23°C8 | ISO 179/1eA | 10 kJ/m² |
| Impact strength of cantilever beam gap | 23°C10 | ISO 180/1A | 8.0 kJ/m² |
| 23°C11 | ISO 180/1A | 10 kJ/m² |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/505R |
|---|---|---|---|
| ball-indentation hardness | H358/30 | ISO 2039-1 | 115 Mpa |
| thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/505R |
|---|---|---|---|
| RTI Elec | UL 746 | 130 °C | |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 8.5E-05 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 143 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 138 °C | |
| 1.8MPa,Unannealed,100mmSpan，HDT | ISO 75-2/Ae | 136 °C | |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
| Heat Deflection Temperature | 0.45MPa,Unannealed,100mmSpan，HDT | ISO 75-2/Be | 144 °C |
| vicat | ASTM D152514 | 149 °C | |
| RTI Str | UL 746 | 130 °C | |
| Linear coefficient of thermal expansion | TD：23to80°C | ISO 11359-2 | 7E-05 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,Annealed，HDT | ISO 75-2/Ae | 136 °C |
| vicat | -- | ISO 306/B120 | 143 °C |
| RTI Imp | UL 746 | 130 °C | |
| Linear coefficient of thermal expansion | MD：23到80°C | ISO 11359-2 | 4E-05 cm/cm/°C |
| vicat | -- | ISO 306/B50 | 141 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 4.7E-05 cm/cm/°C |
| thermal conductivity | ISO 8302 | 0.21 W/m/K |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/505R |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 3300 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 63.0 Mpa |
| elongation | 屈服 | ASTM D638 | 3.0 % |
| Tensile strain | 屈服 | ISO 527-2/5 | 5.0 % |
| bending strength | Break,50.0mmSpan | ASTM D790 | 108 Mpa |
| tensile strength | Break | ASTM D638 | 48.0 Mpa |
| 断裂 | ISO 527-2/5 | 45.0 Mpa | |
| Tensile modulus | ASTM D638 | 3930 Mpa | |
| elongation | 断裂 | ASTM D638 | 12 % |
| bending strength | ISO 178 | 95.0 Mpa | |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | 内部方法 | 11.0 mg |
| Tensile strain | 断裂 | ISO 527-2/5 | 7.0 % |
| flexural modulus | ISO 178 | 3400 Mpa | |
| tensile strength | 屈服 | ISO 527-2/5 | 60.0 Mpa |
| flexural modulus | 50.0mmSpan | ASTM D790 | 3530 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/505R |
|---|---|---|---|
| relative permittivity | 60Hz | IEC 60250 | 2.90 |
| dielectric strength | 0.800mm,在油中 | IEC 60243-1 | 33 KV/mm |
| relative permittivity | 50Hz | IEC 60250 | 2.90 |
| volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| dielectric strength | 1.60mm,在油中 | IEC 60243-1 | 25 KV/mm |
| 3.20mm,在油中 | IEC 60243-1 | 16 KV/mm | |
| relative permittivity | 1MHz | IEC 60250 | 2.80 |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Dissipation Factor | 60Hz | IEC 60250 | 1E-03 |
| 1MHz | IEC 60250 | 0.010 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V | |
| Dissipation Factor | 50Hz | IEC 60250 | 1E-03 |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE US/505R |
|---|---|---|---|
| shrinkage rate | MD：--2 | 内部方法 | 0.20-0.60 % |
| density | ISO 1183 | 1.25 g/cm³ | |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 7.00 cm3/10min |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.31 % |
| 平衡,23°C,50%RH | ISO 62 | 0.13 % | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 7.0 g/10min |
| density | ASTM D792 | 1.26 g/cm³ | |
| shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/505R |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | 5VA |
| Hot filament ignition temperature | 1.0mm | IEC 60695-2-13 | 825 °C |
| Burning wire flammability index | 1.0mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| Limiting Oxygen Index | ISO 4589-2 | 37 % |