PA66 Kinta NI6600 Kinta Technology (Hong Kong) Co., Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Kinta Technology (Hong Kong) Co., Ltd./Kinta NI6600 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 90.0 kJ/m² |
| hardness | Test Condition | Test Method | Kinta Technology (Hong Kong) Co., Ltd./Kinta NI6600 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 112 |
| Electrical performance | Test Condition | Test Method | Kinta Technology (Hong Kong) Co., Ltd./Kinta NI6600 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1E+16 ohms·cm | |
| dielectric strength | ASTM D149 | 20 kV/mm | |
| Dissipation Factor | 23°C,1MHz | ASTM D150 | 0.020 |
| arc resistance | ASTM D495 | 130 sec |
| Mechanical properties | Test Condition | Test Method | Kinta Technology (Hong Kong) Co., Ltd./Kinta NI6600 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 60 % |
| tensile strength | ASTM D638 | 48.0 MPa | |
| Flexural modulus | ASTM D790 | 1450 MPa | |
| bending strength | ASTM D790 | 60.0 MPa |
| flammability | Test Condition | Test Method | Kinta Technology (Hong Kong) Co., Ltd./Kinta NI6600 |
|---|---|---|---|
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| physical property | Test Condition | Test Method | Kinta Technology (Hong Kong) Co., Ltd./Kinta NI6600 |
|---|---|---|---|
| Shrinkage rate | MD：3.00mm | ASTM D955 | 0.60to1.0 % |
| Water absorption rate | 23°C,24hr | ASTM D570 | 1.2 % |
| density | ASTM D792 | 1.07 g/cm³ |
| Thermal performance | Test Condition | Test Method | Kinta Technology (Hong Kong) Co., Ltd./Kinta NI6600 |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD | ASTM D696 | 2.0E-5到3.0E-5 cm/cm/°C |
| melting temperature | DSC | 250 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 70.0 °C |