PC EFT2200 MITSUBISHI ENGINEERING JAPAN
IUPILON™
Casters、Home appliance components
UV resistance、Flame retardant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/EFT2200 |
|---|---|---|---|
| Surface Resistivity | ASTM D257/IEC 60093 | 6.0E+15 Ω | |
| Volume resistivity | ASTM D257/IEC 60093 | 3.0E+16 Ω.cm |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/EFT2200 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 97.0 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 2350 kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | ASTM D638/ISO 527 | 2400 kg/cm²(MPa)[Lb/in²] | |
| elongation at break | ASTM D638/ISO 527 | 6.0 % | |
| tensile strength | ASTM D638/ISO 527 | 63.0 kg/cm²(MPa)[Lb/in²] |
| other | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/EFT2200 |
|---|---|---|---|
| characteristic | 磷含量低、无溴、阻燃性能 | ||
| notes | 以上加工数据.为参考值.以生产厂商设备的实际状况而进行调整 | ||
| Color | 清晰透明 |
| Physical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/EFT2200 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.50-0.70 % | |
| Water absorption rate | ASTM D570/ISO 62 | 0.24 % |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/EFT2200 |
|---|---|---|---|
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 136 ℃（℉） |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 0.000065 mm/mm.℃ |