PC/PBT SABIC INNOVATIVE US X8300MR

Injection grade

US$ 3,750 / MT

FOB Guangzhou port, China

optical performance	Test Condition	Test Method	SABIC INNOVATIVE US/X8300MR
Refractive index		ISO 489	1.539
turbidity	2540 μm	ASTM D1003	1.0 %
transmissivity	2540 μm	ASTM D1003	88.0 %
thermal performance	Test Condition	Test Method	SABIC INNOVATIVE US/X8300MR
Linear coefficient of thermal expansion	Flow : 23 to 60°C	ISO 11359-2	9.0E-5 cm/cm/°C
		Across Flow : -40 to 40°C	ASTM E831	1.1E-4 cm/cm/°C
		Across Flow : 23 to 60°C	ISO 11359-2	9.0E-5 cm/cm/°C
		Across Flow : -40°C	ISO 11359-2	1.1E-4 cm/cm/°C
Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span9	ISO 75-2/Ae	80.0 °C
		1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span8	ISO 75-2/Af	78.0 °C
		0.45 MPa, Unannealed, 3.20 mm	ASTM D648	79.0 °C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	1.1E-4 cm/cm/°C
thermal conductivity		ISO 8302	0.23 W/m/K
Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	75.0 °C
Vicat softening temperature	--	ISO 306/B120	96.0 °C
Ball Pressure Test	85°C	IEC 60695-10-2	通过
Vicat softening temperature	--	ASTM D152510	91.0 °C
injection	Test Condition	Test Method	SABIC INNOVATIVE US/X8300MR
Back pressure			0.200 to 0.500 Mpa
Temperature at the front of the material cylinder			245 to 265 °C
Screw speed			20 to 100 rpm
Mold temperature			45 to 60 °C
Processing (melt) temperature			245 to 265 °C
Suggested injection volume			40 to 80 %
Suggested maximum moisture content			0.020 %
Spray nozzle temperature			245 to 265 °C
Exhaust hole depth			0.013 to 0.020 mm
drying temperature			65 to 75 °C
Temperature in the middle of the barrel			240 to 260 °C
drying time			3.0 to 5.0 hr
Temperature at the rear of the barrel			240 to 250 °C
mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE US/X8300MR
bending strength	--5,6	ISO 178	78.0 Mpa
Bending modulus	50.0 mm Span4	ASTM D790	1680 Mpa
bending strength	Yield, 50.0 mm Span4	ASTM D790	71.0 Mpa
elongation	Break	ISO 527-2/50	> 200 %
		Yield3	ASTM D638	5.0 %
		Yield	ISO 527-2/50	> 5.0 %
		Break3	ASTM D638	150 %
tensile strength	Break	ISO 527-2/50	54.0 Mpa
		Yield	ISO 527-2/50	55.0 Mpa
		Yield3	ASTM D638	47.0 Mpa
Tensile modulus	--2	ASTM D638	1520 Mpa
Tensile modulus		--	ISO 527-2/1	1600 Mpa
Bending modulus	--5	ISO 178	1700 Mpa
tensile strength	Break3	ASTM D638	46.0 Mpa
Physical properties	Test Condition	Test Method	SABIC INNOVATIVE US/X8300MR
melt mass-flow rate	265°C/2.16 kg	ASTM D1238	15 g/10 min
Shrinkage rate	Across FlowFlow : 3.20 mm	Internal Method	0.40 - 0.60 %
Water absorption rate	Saturation, 23°C	ISO 62	0.050 %
Shrinkage rate	Flow : 3.20 mm	Internal Method	0.50 - 0.80 %
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.20 %
Melt Volume Flow Rate (MVR)	265°C/2.16 kg	ISO 1133	15.0 cm3/10min
Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE US/X8300MR
Compared to the anti leakage trace index		UL 746	PLC 0
Surface resistivity		ASTM D257	> 1.0E+15 ohms
Volume resistivity		ASTM D257	> 1.0E+15 ohms·cm
hardness	Test Condition	Test Method	SABIC INNOVATIVE US/X8300MR
Shore hardness	Shore D, 10 Sec	ASTM D2240	73
flammability	Test Condition	Test Method	SABIC INNOVATIVE US/X8300MR
UL flame retardant rating	3.0 mm	UL 94	V-2
Burning wire flammability index	1.0 mm	IEC 60695-2-12	750 °C
impact performance	Test Condition	Test Method	SABIC INNOVATIVE US/X8300MR
Dart impact	23°C, Total Energy	ASTM D3763	95.0 J