Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
LDPE HP20023 EXXONMOBIL SAUDI
ExxonMobil™
Seals、Color masterbatch carrier
No additives、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | EXXONMOBIL SAUDI/HP20023 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | ASTM D256 | 500 J/m |
| hardness | Test Condition | Test Method | EXXONMOBIL SAUDI/HP20023 |
|---|---|---|---|
| Shore hardness | 邵氏 D | ISO 868 | 45 |
| Mechanical properties | Test Condition | Test Method | EXXONMOBIL SAUDI/HP20023 |
|---|---|---|---|
| tensile strength | 屈服, 注塑 | ASTM D638 | 8.00 Mpa |
| elongation | 断裂, 注塑 | ASTM D638 | 150 % |
| bending strength | ASTM D790 | 7.00 Mpa | |
| tensile strength | 断裂, 注塑 | ASTM D638 | 9.00 Mpa |
| Flexural modulus | ASTM D790 | 175 Mpa | |
| Tensile modulus | 注塑，1% 正割 | ASTM D638 | 225 Mpa |
| physical property | Test Condition | Test Method | EXXONMOBIL SAUDI/HP20023 |
|---|---|---|---|
| Environmental stress cracking resistance | 100% Igepal, F50 | ASTM D1693B | 6.00 hr |
| melt mass-flow rate | 190°C/2.16 kg | ASTM D1238 | 20 g/10 min |
| Environmental stress cracking resistance | 10% Igepal, F50 | ASTM D1693B | 2.00 hr |
| Thermal performance | Test Condition | Test Method | EXXONMOBIL SAUDI/HP20023 |
|---|---|---|---|
| vicat | ASTM D1525 | 92.0 °C | |
| melting temperature | 内部方法 | 112 °C | |
| Crystallization peak temperature | ISO 11357-3 | 98 °C |