Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
TSC 1M Hong Kong Huayi
--
--
Before injecting highly transparent TSC-M materials, thoroughly clean the machine with GPPS (especially if the machine has produced transparent ABS, transparent HIPS, acrylic, SAN materials, etc.) to ensure that there are no residual materials in the barrel that affect the highest transparency of TSC-M
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | Hong Kong Huayi/1M |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D-256 | 7.5 kg.cm/cm | |
| transmittance | ASTM D-1003 | 92% 1/8" | |
| Haze ratio | ASTM D-1003 | 1.2 |
| Mechanical properties | Test Condition | Test Method | Hong Kong Huayi/1M |
|---|---|---|---|
| bending strength | ASTM D-790 | 50 MPa | |
| Flexural modulus | ASTM D-790 | 1678 MPa | |
| elongation at break | ASTM D-638 | 85 % | |
| tensile strength | ASTM D-638 | 35 MPa |
| physical property | Test Condition | Test Method | Hong Kong Huayi/1M |
|---|---|---|---|
| Shore hardness | 72 Shore D | ||
| density | ASTM D-792 | 1.03 |
| Thermal performance | Test Condition | Test Method | Hong Kong Huayi/1M |
|---|---|---|---|
| vicat | ASTM D-1525 | 90 ℃ | |
| Heat distortion temperature | HDT | ASTM D-648 | 73 ℃ |
| melt mass-flow rate | ASTM D-1238 | 6 g/10min |