PC/ABS TC-6F UMG JAPAN
UMG ALLOY®
--
Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | UMG JAPAN/TC-6F |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 50 kJ/m² |
| -30°C | ISO 179 | 30 kJ/m² |
| hardness | Test Condition | Test Method | UMG JAPAN/TC-6F |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | ISO 2039-2 | 110 |
| Mechanical properties | Test Condition | Test Method | UMG JAPAN/TC-6F |
|---|---|---|---|
| bending strength | 23°C | ISO 178 | 80.0 Mpa |
| Flexural modulus | 23°C | ISO 178 | 2200 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 2000 Mpa |
| tensile strength | 23°C | ISO 527-2 | 48.0 Mpa |
| flammability | Test Condition | Test Method | UMG JAPAN/TC-6F |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | UMG JAPAN/TC-6F |
|---|---|---|---|
| Shrinkage rate | MD：23°C | ISO 294-4 | 0.50-0.70 % |
| density | 23°C | ISO 1183 | 1.11 g/cm³ |
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 8.50 cm3/10min |
| Thermal performance | Test Condition | Test Method | UMG JAPAN/TC-6F |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/Af | 99.0 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 8.5E-05 cm/cm/°C |