PA66 RFL36XXY SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Car hood、Plastic bag、Electrical appliances、Lighting applications、sporting goods
wear resistant、enhance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/RFL36XXY |
|---|---|---|---|
| Linear thermal expansion coefficient | 流动 : -40 到 40°C | ASTM E831, ISO 11359-2 | 3.8E-5 cm/cm/°C |
| 横向 : -40°C | ISO 11359-2 | 5.5E-5 cm/cm/°C |
| Injection | Test Condition | Test Method | SABIC INNOVATIVE US/RFL36XXY |
|---|---|---|---|
| Suggested Max Moisture | 0.15 到 0.25 % | ||
| Middle Temperature | 280 到 295 °C | ||
| Processing (Melt) Temp | 280 到 305 °C | ||
| Drying Time | 4.0 hr | ||
| Rear Temperature | 265 到 275 °C | ||
| Drying Temperature | 80 °C | ||
| Front Temperature | 295 到 305 °C | ||
| Back Pressure | 0.200 到 0.300 Mpa | ||
| Mold Temperature | 95 到 110 °C | ||
| Screw Speed | 30 到 60 rpm |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/RFL36XXY |
|---|---|---|---|
| Flexural Strength | -- | ISO 178 | 211 Mpa |
| Specific Wear Rate | ASTM D3702 | 2.4E+6 10^-8 mm³/N·m | |
| Flexural Strength | -- | ASTM D790 | 236 Mpa |
| Tensile Elongation | 断裂 | ASTM D638, ISO 527-2 | 2.1 % |
| Coefficient of Friction | Dynamic | ASTM D3702 | 0.58 |
| Tensile Strength | 断裂 | ISO 527-2 | 138 Mpa |
| Flexural Modulus | ISO 178 | 9700 Mpa | |
| Tensile Strength | 断裂 | ASTM D638 | 139 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/RFL36XXY |
|---|---|---|---|
| Instrumented Dart Impact | 23°C, Energy at Peak | ASTM D3763 | 10.0 J |
| -- | ISO 6603-2 | 2.00 J |