Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 HTNFR52G30NH-BK337 DUPONT USA
Zytel®
Automotive sector,Electrical appliances,Electronic field,Electrical field
High temperature resistan,Flame retardant,Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | DUPONT USA/HTNFR52G30NH-BK337 |
|---|---|---|---|
| Odor | VDA270 | 3.50 |
| thermal performance | Test Condition | Test Method | DUPONT USA/HTNFR52G30NH-BK337 |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 283 °C |
| RTI Elec | 0.75mm | UL 746 | 140 °C |
| 1.5mm | UL 746 | 140 °C | |
| 3.0mm | UL 746 | 140 °C | |
| 0.40mm | UL 746 | 140 °C | |
| melting temperature | ISO 11357-3 | 310 °C |
| Electrical performance | Test Condition | Test Method | DUPONT USA/HTNFR52G30NH-BK337 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| dielectric strength | IEC 60243-1 | 33 KV/mm | |
| relative permittivity | 100Hz | IEC 60250 | 4.30 |
| Dissipation Factor | 100Hz | IEC 60250 | 7E-03 |
| volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| relative permittivity | 1MHz | IEC 60250 | 4.00 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.013 |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/HTNFR52G30NH-BK337 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 10000 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 150 Mpa |
| bending strength | ISO 178 | 230 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 2.2 % |
| flexural modulus | ISO 178 | 8700 Mpa |
| Physical properties | Test Condition | Test Method | DUPONT USA/HTNFR52G30NH-BK337 |
|---|---|---|---|
| shrinkage rate | TD | ISO 294-4 | 1.0 % |
| MD | ISO 294-4 | 0.30 % |
| flammability | Test Condition | Test Method | DUPONT USA/HTNFR52G30NH-BK337 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| 0.75mm | IEC 60695-11-10,-20 | V-0 | |
| 1.5mm | IEC 60695-11-10,-20 | V-0 | |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 775 °C |
| FMVSS flammability | FMVSS302 | DNI | |
| Hot filament ignition temperature | 0.40mm | IEC 60695-2-13 | 700 °C |
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| Limiting Oxygen Index | ISO 4589-2 | 37 % | |
| Hot filament ignition temperature | 0.75mm | IEC 60695-2-13 | 725 °C |