PA46 TW271B3 DSM JAPAN
Stanyl®
Automotive Applications,Electronic and electrical components
Thermal stability
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
thermal performance | Test Condition | Test Method | DSM JAPAN/TW271B3 |
---|---|---|---|
Hot deformation temperature | 1.8 MPa, Unannealed | ISO 75-2/A | 290 °C |
Linear coefficient of thermal expansion | Across Flow | ISO 11359-2 | 5.0E-5 cm/cm/°C |
Flow | ISO 11359-2 | 2.5E-5 cm/cm/°C | |
Melting temperature | ISO 11357-3 | 295 °C |
mechanical properties | Test Condition | Test Method | DSM JAPAN/TW271B3 |
---|---|---|---|
Bending modulus | ISO 178 | 11000 Mpa | |
Tensile modulus | 200°C | ISO 527-2 | 5100 Mpa |
-- | ISO 527-2 | 12500 Mpa | |
120°C | ISO 527-2 | 6300 Mpa | |
160°C | ISO 527-2 | 5700 Mpa | |
180°C | ISO 527-2 | 5400 Mpa | |
Tensile strain | Break, 180°C | ISO 527-2 | 5.0 % |
Break, 160°C | ISO 527-2 | 5.0 % | |
Break, 120°C | ISO 527-2 | 5.0 % | |
Break | ISO 527-2 | 2.0 % | |
Break, 200°C | ISO 527-2 | 5.0 % | |
tensile strength | Break, 120°C | ISO 527-2 | 108 Mpa |
Break, 200°C | ISO 527-2 | 76.0 Mpa | |
Break | ISO 527-2 | 185 Mpa | |
Break, 180°C | ISO 527-2 | 84.0 Mpa | |
Break, 160°C | ISO 527-2 | 92.0 Mpa |
Electrical performance | Test Condition | Test Method | DSM JAPAN/TW271B3 |
---|---|---|---|
Volume resistivity | IEC 60093 | 1.0E+3 ohms·cm |
Physical properties | Test Condition | Test Method | DSM JAPAN/TW271B3 |
---|---|---|---|
density | ISO 1183 | 1.32 g/cm³ | |
Shrinkage rate | 横向Flow | ISO 294-4 | 0.80 % |
Flow | ISO 294-4 | 0.20 % | |
Water absorption rate | Equilibrium, 23°C, 50% RH | ISO 62 | 2.6 % |
impact performance | Test Condition | Test Method | DSM JAPAN/TW271B3 |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 6.0 kJ/m² |
-30°C | ISO 179/1eA | 5.5 kJ/m² | |
Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 6.0 kJ/m² |
Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 45 kJ/m² |
23°C | ISO 179/1eU | 50 kJ/m² |
flammability | Test Condition | Test Method | DSM JAPAN/TW271B3 |
---|---|---|---|
Flammability level | UL 94 | HB |