ABS AP-8A A&L SHANGHAI
KRALASTIC®
Home appliance components
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | A&L SHANGHAI/AP-8A |
|---|---|---|---|
| melt mass-flow rate | 220℃/10kg | ASTM D-1238 | 30 g/10min |
| density | 23℃ | ASTM D-792 | 1.04 g/cm |
| Mechanical properties | Test Condition | Test Method | A&L SHANGHAI/AP-8A |
|---|---|---|---|
| Flexural modulus | 23℃ | ASTM D-790 | 2250 Mpa |
| elongation at break | 23℃ | ASTM D-638 | 20 % |
| Impact strength of cantilever beam gap | -30℃,6.4mmt | ASTM D-256 | 118 J/m |
| bending strength | 23℃ | ASTM D-790 | 59 Mpa |
| tensile strength | 23℃ | ASTM D-638 | 44 Mpa |
| Impact strength of cantilever beam gap | 23℃ 6.4mmt | ASTM D-256 | 294 J/m |
| Rockwell hardness | 23℃ | ASTM D-785 | 113 R-Scale |
| processability | Test Condition | Test Method | A&L SHANGHAI/AP-8A |
|---|---|---|---|
| mold temperature | 200-260 °C |
| physical property | Test Condition | Test Method | A&L SHANGHAI/AP-8A |
|---|---|---|---|
| Shrinkage rate | ASTM D-955 | 0.4-0.6 % |
| Thermal performance | Test Condition | Test Method | A&L SHANGHAI/AP-8A |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB calss | |
| vicat | 1.0kgf | ASTM D-1525 | 107 °C |
| Heat distortion temperature | 1.82Mpa，HDT | ASTM D-648 | 88 °C |