PA66 3010N MITSUBISHI ENGINEERING JAPAN
Akulon®
Automotive components,Electronic and electrical components
Low temperature resistanc,wear resistant,Non halogen flame retarda
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/3010N |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO 179 | 3(7) KJ/m | |
| Breaking stress | 80 Mpa | ||
| Tensile modulus | ISO 527-1 | 3500/2100 Mpa | |
| bending strength | D178 | 133(64) Mpa | |
| Flexural modulus | D178 | 3600(1900) Mpa | |
| elongation | 断裂 | 3.2 % |
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/3010N |
|---|---|---|---|
| dielectric strength | IEC 243-1 | 26 MV/m | |
| Dielectric loss | IEC 250 | 0.008(0.019) | |
| dielectric constant | D150 | 4 Pf/m | |
| Compared to the Leakage Traceability Index (CTI) | IEC 112 | ＞600 |
| physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/3010N |
|---|---|---|---|
| Shrinkage rate | 1.3 MD% | ||
| 1.5 TD% | |||
| Water absorption rate | D570 | 2.7 % |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/3010N |
|---|---|---|---|
| Heat distortion temperature | HDT | D648 | 80(231) °C |
| UL flame retardant rating | UL 94 | V-0 |