PC SLX2432T SABIC INNOVATIVE US
LEXAN™
Electronic and Electrical、Lighting applications、Plastic bag、Outdoor applications、Lawn garden equipment
Aging resistance、UV resistance、Antistatic
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/SLX2432T |
|---|---|---|---|
| Linear thermal expansion coefficient | TD：-40到40°C | ISO11359-2 | 6.5E-05 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 116 °C |
| Vicat Softening Temperature | -- | ISO306/B50 | 135 °C |
| Ball PressureTest | 125°C | IEC60695-10-2 | Pass |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 130 °C |
| Linear thermal expansion coefficient | TD：-40到40°C | ASTME831 | 6.5E-05 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 130 °C |
| Linear thermal expansion coefficient | MD：-40到40°C | ISO11359-2 | 6.7E-05 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 118 °C |
| Vicat Softening Temperature | ASTMD152510 | 135 °C | |
| -- | ISO306/B120 | 137 °C | |
| Linear thermal expansion coefficient | MD：-40到40°C | ASTME831 | 6.7E-05 cm/cm/°C |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/SLX2432T |
|---|---|---|---|
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.17 % |
| 24hr | ASTMD570 | 0.12 % | |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50to0.70 % |
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 10 g/10min |
| Outdoor Suitability | UL746C | f1 | |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 9.00 cm3/10min |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.25 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/SLX2432T |
|---|---|---|---|
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 2500 Mpa |
| Tensile Stress | 断裂 | ISO527-2/50 | 69.0 Mpa |
| Tensile Elongation | 断裂 | ASTMD638 | 110 % |
| Tensile Strain | 断裂 | ISO527-2/50 | 110 % |
| Tensile Modulus | ISO527-2/1 | 2550 Mpa | |
| Tensile Strength | 屈服 | ASTMD638 | 67.0 Mpa |
| Flexural Modulus | ISO178 | 2500 Mpa | |
| Flexural Strength | 屈服,50.0mm跨距 | ASTMD790 | 105 Mpa |
| Tensile Elongation | 屈服 | ASTMD638 | 6.0 % |
| Tensile Stress | 屈服 | ISO527-2/50 | 65.0 Mpa |
| Tensile Strain | 屈服 | ISO527-2/50 | 6.0 % |
| Flexural Strength | ISO178 | 105 Mpa | |
| Tensile Modulus | ASTMD638 | 2550 Mpa | |
| Tensile Strength | 断裂 | ASTMD638 | 72.0 Mpa |
| Optical | Test Condition | Test Method | SABIC INNOVATIVE US/SLX2432T |
|---|---|---|---|
| Index of Refraction | ASTMD542 | 1.590 | |
| Transmittance | 2540µm | ASTMD1003 | 84.0 % |
| Haze | 2540µm | ASTMD1003 | 0.80 % |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/SLX2432T |
|---|---|---|---|
| Notched Izod Impact Strength | -30°C | ISO180/1A | 10 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 15 kJ/m² |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 77.0 J |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 30 kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | NoBreak |
| Instrumented Dart Impact | -40°C,TotalEnergy | ASTMD3763 | 85.0 J |
| 23°C | ISO180/1U | NoBreak | |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 25 kJ/m² |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/SLX2432T |
|---|---|---|---|
| GlowWireFlammability | 1.6mm | IEC60695-2-12 | 960 °C |
| Oxygen Index | ISO4589-2 | 38 % | |
| Flame Rating | 1.5mm | UL94 | V-2 |