POM FM130 FPC TAIWAN
FORMOCON® 
Automotive sector、Electrical field、Electronic field、bearing、Engine parts、Pipe fittings、Engine parts、Button
Processability、Low liquidity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodFPC TAIWAN/FM130
Rockwell hardnessM级ASTM D78580
Mechanical propertiesTest ConditionTest MethodFPC TAIWAN/FM130
elongation断裂ASTM D63855 %
bending strengthASTM D79093.2 Mpa
tensile strength 屈服ASTM D63860.8 Mpa
compressive strength1%应变ASTM D69531.4 Mpa
10%应变ASTM D695108 Mpa
Flexural modulusASTM D7902550 Mpa
Electrical performanceTest ConditionTest MethodFPC TAIWAN/FM130
dielectric strength2.00mmASTM D14924 KV/mm
dielectric constant50HzIEC 602503.80
Surface ResistivityASTM D2571E+16 ohms
Volume resistivity23°CASTM D2571E+14 ohms·cm
dielectric constant1MHzIEC 602503.80
1kHzIEC 602503.80
flammabilityTest ConditionTest MethodFPC TAIWAN/FM130
UL flame retardant ratingUL 94HB
physical property Test ConditionTest MethodFPC TAIWAN/FM130
Water absorption rate平衡,23°C,69%RHASTM D5700.22 %
Shrinkage rateMD:3.00mmASTM D9551.8-2.2 %
melt mass-flow rate190°C/2.16kgASTM D123813 g/10min
Thermal performanceTest ConditionTest MethodFPC TAIWAN/FM130
Heat distortion temperature1.8MPa,未退火,HDTASTM D648110 °C
vicatASTM D1525162 °C
Heat distortion temperature0.45MPa,未退火,HDTASTM D648158 °C
Linear coefficient of thermal expansionMDASTM D6968.5E-05 cm/cm/°C
melting temperatureDSC165 °C