PC LUX9616-WH8E492X SABIC INNOVATIVE US
LEXAN™
Plastic bag、Lighting applications
Flame retardant、transparent、optical performance 、Thermal stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/LUX9616-WH8E492X |
|---|---|---|---|
| 1.8MPa, Unannealed,64.0mm Span | ISO75-2/Af | 125 °C | |
| 0.45MPa, Unannealed,3.20mm Span | ISO75-2/Bf | 135 °C | |
| Linear thermal expansion coefficient | MD:-40到40°C | ASTME831 | 6.8E-05 cm/cm/°C |
| 1.8MPa, Unannealed,3.20mm | ASTMD648 | 125 °C | |
| Ball PressureTest | 125°C | IEC60695-10-2 | Pass |
| Vicat Softening Temperature | ASTMD152513 | 141 °C | |
| Linear thermal expansion coefficient | TD:-40到40°C | ASTME831 | 6.7E-05 cm/cm/°C |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/LUX9616-WH8E492X |
|---|---|---|---|
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.15 % |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.60到0.80 % |
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 7.0 g/10min |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.35 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/LUX9616-WH8E492X |
|---|---|---|---|
| ASTMD638 | 2300 Mpa | ||
| Break | ASTMD638 | 65.0 Mpa | |
| fracture | ISO527-2/50 | 75 % | |
| Break | ASTMD638 | 80 % | |
| Yield,50.0mm Span | ASTMD790 | 95.0 Mpa | |
| yield | ISO527-2/50 | 6.0 % | |
| 50.0mm Span | ASTMD790 | 2160 Mpa | |
| Yield | ASTMD638 | 6.0 % | |
| fracture | ISO527-2/50 | 58.0 Mpa | |
| ISO178 | 95.0 Mpa | ||
| Yield | ASTMD638 | 62.0 Mpa | |
| yield | ISO527-2/50 | 62.0 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/LUX9616-WH8E492X |
|---|---|---|---|
| ASTMD256 | 150 J/m | ||
| ISO180/1A | 15 kJ/m² | ||
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 70.0 J |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/LUX9616-WH8E492X |
|---|---|---|---|
| Glow Wire Ignition Temperature | 1.00mm | IEC60695-2-13 | 850 °C |
| Glow Wire Flammability Index | 1.00mm | IEC60695-2-12 | 960 °C |
| Glow Wire Ignition Temperature | 1.50mm | IEC60695-2-13 | 850 °C |
| Flame Rating | 1.50mm | UL94 | V-0 |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/LUX9616-WH8E492X |
|---|---|---|---|
| High Amp Arc Ignition | HAI | UL746 | PLC 1 |
| Hot-wire Ignition | HWI | UL746 | PLC 3 |
| Comparative Tracking Index | CTI | UL746 | PLC 3 |