HDPE FB1520 BOREALIS EUROPE
Borstar®
film,Charger casing,Bag,Protective Coatings,Food packaging
High rigidity,high strength,antioxidant,Processability,Food contact compliance,High toughness
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Other performance | Test Condition | Test Method | BOREALIS EUROPE/FB1520 |
---|---|---|---|
film thickness | 15 µm | ||
Thin film puncture strength | 15.0μm | ASTM D-5748 | 30 N |
15.0μm | ASTM D-5748 | 0.7 J |
Basic Performance | Test Condition | Test Method | BOREALIS EUROPE/FB1520 |
---|---|---|---|
density | ASTM D-1505 | 0.952 g/m3 | |
melt mass-flow rate | 190℃/21.6kg | ASTM D-1238 | 7 g/10min |
190℃/2.16 kg | ASTM D-1238 | <0.10 g/10min | |
190℃/5.0kg | ASTM D-1238 | 0.25 g/10min |
thermal performance | Test Condition | Test Method | BOREALIS EUROPE/FB1520 |
---|---|---|---|
Melting temperature | ISO 11357-3 | 133 °C | |
271 ℃(℉) | |||
Melt Temperature | 210-230 °C | ||
Vicat softening temperature | ASTM D1525/ISO R306 | 264 F ℃(℉) | |
ISO 306 | 129 °C |
mechanical properties | Test Condition | Test Method | BOREALIS EUROPE/FB1520 |
---|---|---|---|
Elmendorf tear strength | 15.0μm,MD | ASTM D-1922 | 20 |
15.0μm,TD | ASTM D-1922 | 40 g | |
Elongation at Break | 15.0μm,MD | ASTM D-882 | 350 % |
15.0μm,TD | ASTM D-882 | 450 | |
Environmental stress cracking resistance | 10% Igepal,F50 | ASTM D-1693 | >1000 hr |
Secant modulus | 15.0μm,TD | ASTM D-882 | 900 |
15.0μm,MD | ASTM D-882 | 750 Mpa | |
tensile strength | Yield,15.0μm | ASTM D-882 | 35 Mpa |
15.0μm,TD,Break | ASTM D-882 | 95 | |
15.0μm,MD,Break | ASTM D-882 | 100 |
other | Test Condition | Test Method | BOREALIS EUROPE/FB1520 |
---|---|---|---|
characteristic | 刚性高、抗氧化、可加工性良好、食品接触 | ||
purpose | 保护涂料、衬里、袋子、薄膜 | ||
remarks | 颗粒料 |
Physical properties | Test Condition | Test Method | BOREALIS EUROPE/FB1520 |
---|---|---|---|
density | ASTM D792/ISO 1183 | 0.952 | |
melt mass-flow rate | ASTM D1238/ISO 1133 | <0.25 g/10min |