PA6 Polimid B 30 GB Poliblend S.p.a.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Poliblend S.p.a./Polimid B 30 GB |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO 180/A | 4.5 kJ/m² | |
| Suspended wall beam without notch impact strength | ISO 180 | 40 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Poliblend S.p.a./Polimid B 30 GB |
|---|---|---|---|
| Tensile strain | 断裂 | ISO 527-2 | 8.0 % |
| Tensile modulus | ISO 527-2 | 4200 MPa | |
| tensile strength | 断裂 | ISO 527-2 | 70.0 MPa |
| Tensile strain | 屈服 | ISO 527-2 | 3.5 % |
| tensile strength | 屈服 | ISO 527-2 | 70.0 MPa |
| Electrical performance | Test Condition | Test Method | Poliblend S.p.a./Polimid B 30 GB |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 1 |
| flammability | Test Condition | Test Method | Poliblend S.p.a./Polimid B 30 GB |
|---|---|---|---|
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| 0.8mm | UL 94 | HB | |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 650 °C |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | Poliblend S.p.a./Polimid B 30 GB |
|---|---|---|---|
| Shrinkage rate | 0.90to1.3 % | ||
| Water absorption rate | 23°C,24hr | ISO 62 | 0.90 % |
| density | ISO 1183 | 1.35 g/cm³ |
| Thermal performance | Test Condition | Test Method | Poliblend S.p.a./Polimid B 30 GB |
|---|---|---|---|
| Heat distortion temperature | 连续使用温度2，HDT | 110 °C | |
| vicat | ISO 306/A120 | 205 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 195 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 95.0 °C | |
| ball-indentation hardness | 165°C | IEC 60695-10-2 | 通过 |
| melting temperature | DSC | 222 °C |