PBT TAROLOX 10 Z2 Taro Plast S.p.A.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Taro Plast S.p.A./TAROLOX 10 Z2 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 10 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 45 J/m |
| 23°C | ASTM D256 | 85 J/m |
| Electrical performance | Test Condition | Test Method | Taro Plast S.p.A./TAROLOX 10 Z2 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| dielectric strength | 2.00mm | IEC 60243-1 | 18 kV/mm |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 0 |
| Mechanical properties | Test Condition | Test Method | Taro Plast S.p.A./TAROLOX 10 Z2 |
|---|---|---|---|
| Flexural modulus | ISO 178 | 2100 MPa | |
| Tensile strain | 断裂 | ISO 527-2/50 | >100 % |
| Tensile modulus | ISO 527-2/1 | 2200 MPa | |
| tensile strength | 屈服 | ISO 527-2/50 | 55.0 MPa |
| bending strength | ISO 178 | 70.0 MPa | |
| tensile strength | 断裂 | ISO 527-2/50 | 45.0 MPa |
| flammability | Test Condition | Test Method | Taro Plast S.p.A./TAROLOX 10 Z2 |
|---|---|---|---|
| UL flame retardant rating | 1.0mm | UL 94 | HB |
| 3.2mm | UL 94 | HB | |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 650 °C |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| Limiting Oxygen Index | ASTM D2863 | 22 % |
| physical property | Test Condition | Test Method | Taro Plast S.p.A./TAROLOX 10 Z2 |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 1.6to1.8 % |
| melt mass-flow rate | 250°C/1.2kg | ISO 1133 | 12 g/10min |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.080 % |
| GranuleHumidity | 内部方法 | <0.050 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.50 % |
| Shrinkage rate | TD | 内部方法 | 1.6to1.8 % |
| density | ISO 1183 | 1.26to1.28 g/cm³ |
| Thermal performance | Test Condition | Test Method | Taro Plast S.p.A./TAROLOX 10 Z2 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 218 °C | |
| Linear coefficient of thermal expansion | MD：-30到30°C | ISO 11359-2 | 1E-04 cm/cm/°C |
| vicat | -- | ISO 306/A50 | 185 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 55.0 °C |
| vicat | -- | ISO 306/B50 | 165 °C |
| ball-indentation hardness | 165°C | IEC 60695-10-2 | 通过 |