ABS+PMMA Abstron IPM 2000 Bhansali Engineering Polymers Limited
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Bhansali Engineering Polymers Limited/Abstron IPM 2000 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,6.40mm,注塑 | ASTM D256 | 120 J/m |
| 23°C,3.20mm,注塑 | ASTM D256 | 150 J/m |
| hardness | Test Condition | Test Method | Bhansali Engineering Polymers Limited/Abstron IPM 2000 |
|---|---|---|---|
| Rockwell hardness | R级,注塑 | ASTM D785 | 110 |
| Hardness | ASTM D3363 | HB |
| Mechanical properties | Test Condition | Test Method | Bhansali Engineering Polymers Limited/Abstron IPM 2000 |
|---|---|---|---|
| Flexural modulus | 6.40mm,注塑 | ASTM D790 | 2300 MPa |
| bending strength | 屈服,6.40mm,注塑 | ASTM D790 | 65.7 MPa |
| tensile strength | 屈服,3.20mm,注塑 | ASTM D638 | 51.0 MPa |
| flammability | Test Condition | Test Method | Bhansali Engineering Polymers Limited/Abstron IPM 2000 |
|---|---|---|---|
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| physical property | Test Condition | Test Method | Bhansali Engineering Polymers Limited/Abstron IPM 2000 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.30to0.50 % |
| density | ASTM D792 | 1.07 g/cm³ | |
| melt mass-flow rate | 220°C/10.0kg | ASTM D1238 | 20 g/10min |
| Thermal performance | Test Condition | Test Method | Bhansali Engineering Polymers Limited/Abstron IPM 2000 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,退火,6.40mm,注塑，HDT | ASTM D648A | 92.0 °C |