Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC C6200-111 SABIC INNOVATIVE NANSHA
CYCOLOY™
Automotive sector、Household appliances、Electronic field、Electrical field
heat-resisting、High temperature resistan、High impact resistance、High mobility、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/C6200-111 |
|---|---|---|---|
| Dart impact | -30°C,EnergyatPeakLoad | ASTM D3763 | 54.2 J |
| 23°C,EnergyatPeakLoad | ASTM D3763 | 61.0 J |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/C6200-111 |
|---|---|---|---|
| relative permittivity | 60Hz | IEC 60250 | 2.80 |
| dielectric strength | 0.800mm,在油中 | IEC 60243-1 | 35 KV/mm |
| relative permittivity | 50Hz | IEC 60250 | 2.80 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
| dielectric strength | 3.20mm,在油中 | IEC 60243-1 | 17 KV/mm |
| relative permittivity | 1MHz | IEC 60250 | 2.70 |
| Dissipation Factor | 50Hz | IEC 60250 | 4E-03 |
| 60Hz | IEC 60250 | 4E-03 | |
| 1MHz | IEC 60250 | 8E-03 | |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 3 |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 2 |
| dielectric strength | 1.60mm,在油中 | IEC 60243-1 | 25 KV/mm |
| arc resistance | ASTM D495 | PLC6 | |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/C6200-111 |
|---|---|---|---|
| Flexural modulus | 100mmSpan | ASTM D790 | 2690 Mpa |
| elongation | 断裂 | ASTM D638 | 50 % |
| bending strength | Yield,100mmSpan | ASTM D790 | 103 Mpa |
| tensile strength | 屈服 | ASTM D638 | 66.9 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/C6200-111 |
|---|---|---|---|
| UL flame retardant rating | 3.4mm | UL 94 | 5VA |
| 2.0mm | UL 94 | 5VB | |
| 1.2mm | UL 94 | V-1 | |
| 1.5mm | UL 94 | V-0 | |
| 0.71mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/C6200-111 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.40-0.60 % |
| melt mass-flow rate | 260°C/2.16kg | ASTM D1238 | 15 g/10min |
| spiral flow length | 内部方法 | 68.6 CM | |
| Shrinkage rate | TD：3.20mm | 内部方法 | 0.40-0.60 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/C6200-111 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 90.6 °C |
| RTI Imp | UL 746 | 85.0 °C | |
| RTI Str | UL 746 | 85.0 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 87.8 °C |
| RTI Elec | UL 746 | 85.0 °C |