Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS Lupoy® HR5007A LG Chem Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LG Chem Ltd./Lupoy® HR5007A |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eU2 | NoBreak |
| 23°C | ISO 179/1eU2 | NoBreak | |
| 23°C | ISO 179/1eA2 | NoBreak | |
| -30°C | ISO 179/1eA2 | 36.3 kJ/m² | |
| Impact strength of cantilever beam gap | ASTM D256 | NoBreak | |
| 23°C,3.20mm,注塑 | ASTM D256 | 640 J/m | |
| -30°C,3.20mm,注塑 | ASTM D256 | 490 J/m |
| hardness | Test Condition | Test Method | LG Chem Ltd./Lupoy® HR5007A |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 114 |
| Mechanical properties | Test Condition | Test Method | LG Chem Ltd./Lupoy® HR5007A |
|---|---|---|---|
| Tensile strain | Break,3.20mm,InjectionMolded | ASTM D638 | >100 % |
| Tensile modulus | ISO 527-22 | 2200 MPa | |
| Nominal fracture strain | ISO 527-22 | >50 % | |
| Tensile strain | 屈服 | ISO 527-22 | 4.9 % |
| bending strength | 3.20mm | ASTM D790 | 77.5 MPa |
| tensile strength | 屈服 | ISO 527-22 | 60.0 MPa |
| 屈服,3.20mm,注塑 | ASTM D638 | 56.9 MPa | |
| Flexural modulus | 3.20mm,InjectionMolded | ASTM D790 | 2110 MPa |
| Electrical performance | Test Condition | Test Method | LG Chem Ltd./Lupoy® HR5007A |
|---|---|---|---|
| Volume resistivity | IEC 600932 | >1.0E+13 ohms·m | |
| Hot wire ignition (HWI) | 1.6mm | UL 746 | PLC 3 |
| High arc combustion index (HAI) | 1.6mm | UL 746 | PLC 1 |
| Dissipation Factor | 1MHz | IEC 602502 | 0.010 |
| Surface Resistivity | IEC 600932 | 3.8E+14 ohms | |
| Hot wire ignition (HWI) | 3.0mm | UL 746 | PLC 3 |
| High arc combustion index (HAI) | 3.0mm | UL 746 | PLC 1 |
| High Voltage Arc Traceability Rate (HVTR) | PLC | UL 746 | |
| relative permittivity | 1MHz | IEC 602502 | 2.80 |
| Compared to the Leakage Tracking Index (CTI) | IEC 601122 | PLC 3 | |
| arc resistance | ASTM D495 | PLC6 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 0 |
| dielectric strength | IEC 60243-12 | 42 kV/mm |
| flammability | Test Condition | Test Method | LG Chem Ltd./Lupoy® HR5007A |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | LG Chem Ltd./Lupoy® HR5007A |
|---|---|---|---|
| melt mass-flow rate | 250°C/2.16kg | ASTM D1238 | 5.3 g/10min |
| Water absorption rate | 饱和 | ISO 622 | 0.15 % |
| Shrinkage rate | MD：3.20mm,InjectionMolded | ASTM D955 | 0.50to0.80 % |
| Melt volume flow rate | 260°C/5.0kg | ISO 11332 | 18.0 cm³/10min |
| density | ASTM D792 | 1.14 g/cm³ | |
| ISO 11832 | 1130 kg/m³ |
| Thermal performance | Test Condition | Test Method | LG Chem Ltd./Lupoy® HR5007A |
|---|---|---|---|
| vicat | 50N | ISO 3062 | 119 °C |
| Linear coefficient of thermal expansion | TD | ISO 11359-22 | 8.3E-05 cm/cm/°C |
| MD | ISO 11359-22 | 7.7E-05 cm/cm/°C | |
| RTI Imp | 1.6mm | UL 746 | 60.0 °C |
| Heat distortion temperature | 1.8MPa，HDT | ISO 75-22 | 104 °C |
| RTI Str | 1.6mm | UL 746 | 60.0 °C |
| 3.0mm | UL 746 | 60.0 °C | |
| Glass Transition Temperature | ISO 11357-22 | 150 °C | |
| Heat distortion temperature | 1.8MPa,Unannealed,6.40mm,InjectionMolded，HDT | ASTM D648 | 113 °C |
| RTI Elec | 1.6mm | UL 746 | 60.0 °C |
| 3.0mm | UL 746 | 60.0 °C | |
| RTI Imp | 3.0mm | UL 746 | 60.0 °C |