Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 1154W TORAY JAPAN
Toraycon®
Electrical components
Flame retardant,Low warpage
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | TORAY JAPAN/1154W |
|---|---|---|---|
| BarFlowLength | 250°C,1.00mm | 内部方法 | 101 mm |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/1154W |
|---|---|---|---|
| dielectric constant | 23°C,50Hz | IEC 60250 | 4.00 |
| 23°C,1kHz | IEC 60250 | 3.70 | |
| dielectric strength | IEC 60243-1 | 19 KV/mm | |
| Volume resistivity | IEC 60093 | 6.4E+16 ohms·cm | |
| arc resistance | IEC 60950 | 125 sec | |
| Dissipation Factor | 23°C,50Hz | IEC 60250 | 2E-03 |
| 23°C,1MHz | IEC 60250 | 0.020 |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/1154W |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2 | 2.5 % |
| bending strength | 23°C | ISO 178 | 170 Mpa |
| Flexural modulus | 23°C | ISO 178 | 9200 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 9800 Mpa |
| tensile strength | 23°C | ISO 527-2 | 105 Mpa |
| flammability | Test Condition | Test Method | TORAY JAPAN/1154W |
|---|---|---|---|
| UL flame retardant rating | 0.79mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | TORAY JAPAN/1154W |
|---|---|---|---|
| Shrinkage rate | MD:3.00mm4 | 内部方法 | 0.40 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.070 % |
| Shrinkage rate | TD:3.00mm3 | 内部方法 | 0.60 % |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/1154W |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 218 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 194 °C | |
| Linear coefficient of thermal expansion | MD：-30到100°C | ISO 11359-2 | 3.7E-05 cm/cm/°C |