Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PP BHC5012C BOREALIS EUROPE
Borealis
Automotive sector,Shell,Parts under the hood of a car
Thermal stability,Easy to process,copolymer,Filler: Copper filler
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BOREALIS EUROPE/BHC5012C |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C,注塑 | ISO 179/1eU | NoBreak |
| -20°C,注塑 | ISO 179/1eU | NoBreak | |
| Impact strength of cantilever beam gap | 23°C,注塑 | ISO 180/1A | 55 kJ/m² |
| Charpy Notched Impact Strength | -20°C,注塑 | ISO 179/1eA | 4.5 kJ/m² |
| 23°C,注塑 | ISO 179/1eA | 75 kJ/m² | |
| Impact strength of cantilever beam gap | -20°C,注塑 | ISO 180/1A | 5.5 kJ/m² |
| Charpy Notched Impact Strength | -30°C,注塑 | ISO 179/1eA | 3.8 kJ/m² |
| Mechanical properties | Test Condition | Test Method | BOREALIS EUROPE/BHC5012C |
|---|---|---|---|
| Tensile modulus | 注塑 | ISO 527-2/1 | 1150 Mpa |
| bending strength | 注塑 | ISO 178 | 35.0 Mpa |
| Tensile strain | 屈服,注塑 | ISO 527-2/50 | 11 % |
| Flexural modulus | 注塑 | ISO 178 | 1350 Mpa |
| tensile strength | 屈服,注塑 | ISO 527-2/50 | 27.0 Mpa |
| physical property | Test Condition | Test Method | BOREALIS EUROPE/BHC5012C |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 1.9 % |
| density | ISO 1183 | 0.905 g/cm³ | |
| melt mass-flow rate | 230°C/2.16kg | ISO 1133 | 0.30 g/10min |
| Thermal performance | Test Condition | Test Method | BOREALIS EUROPE/BHC5012C |
|---|---|---|---|
| MeltEnergy | ISO 11357 | 86.8 kJ/kg | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 80.0 °C |
| vicat | ISO 306/B50 | 65.0 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 50.0 °C |