POM KAL-4022 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Automotive Applications
heat-resisting,high strength,Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/KAL-4022 |
|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO 75-2/Af | 87.0 °C |
| 1.8MPa,未退火,3.20mm | ASTM D648 | 132 °C | |
| 0.45MPa,未退火,3.20mm | ASTM D648 | 162 °C |
| mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/KAL-4022 |
|---|---|---|---|
| Bending modulus | 50.0mmSpan | ASTM D790 | 3090 Mpa |
| ISO 178 | 3080 Mpa | ||
| bending strength | ISO 178 | 77.0 Mpa | |
| elongation | 断裂 | ASTM D638 | 7.4 % |
| 屈服 | ASTM D638 | 6.5 % | |
| Friction coefficient | Dynamic | ASTM D3702Modified | 0.23 |
| Static | ASTM D3702Modified | 0.16 | |
| Tensile modulus | ASTM D638 | 3640 Mpa | |
| ISO 527-2/1 | 3460 Mpa | ||
| Tensile strain | 断裂 | ISO 527-2/5 | 7.4 % |
| 屈服 | ISO 527-2/5 | 6.3 % | |
| tensile strength | 断裂 | ISO 527-2/5 | 56.0 Mpa |
| 屈服 | ISO 527-2/5 | 57.0 Mpa | |
| Break | ASTM D638 | 58.0 Mpa | |
| Wear factor | Ring | ASTM D3702Modified | 0.00 10^-10in^5-min/ft-lb-hr |
| Washer | ASTM D3702Modified | 8.00 10^-10in^5-min/ft-lb-hr |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE US/KAL-4022 |
|---|---|---|---|
| Shrinkage rate | TD：24hr | ASTM D955 | 2.0-4.0 % |
| MD：24hr | ASTM D955 | 2.0-4.0 % | |
| MD：--2 | Internal Method | 1.8-2.2 % |
| impact performance | Test Condition | Test Method | SABIC INNOVATIVE US/KAL-4022 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 5.5 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 32 kJ/m² |