PA66
PA66 ASCEND USA R550 NAT
Food grade
US$ 4,180 / MT
FOB Dongguan Port
mechanical propertiesTest ConditionTest MethodASCEND USA/R550 NAT
Poisson's ratioISO 527-20.40
bending strength23°CISO 178350 Mpa
tensile strengthBreak,23°CISO 527-2240 Mpa
Bending modulus23°CISO 17816000 Mpa
Tensile modulus23°CISO 527-216800 Mpa
Tensile strainBreak,23°CISO 527-22.5 %
flammabilityTest ConditionTest MethodASCEND USA/R550 NAT
UL flame retardant rating0.75mmUL 94HB
3.0mmUL 94HB
1.5mmUL 94HB
Physical propertiesTest ConditionTest MethodASCEND USA/R550 NAT
Water absorption rate23°C,24hrISO 620.50 %
Shrinkage rateMD:23°C,2.00mmISO 294-40.40 %
Water absorption rateEquilibrium,23°C,50%RHISO 621.2 %
Shrinkage rateTD:23°C,2.00mmISO 294-40.90 %
Electrical performanceTest ConditionTest MethodASCEND USA/R550 NAT
High arc combustion index1.5mmUL 746PLC 0
Dielectric strength1.00mmIEC 6024322 KV/mm
High arc combustion index0.75mmUL 746PLC 0
High voltage arc tracing rateHVTRUL 746PLC 1
Volume resistivity0.750mmIEC 600931E+13 ohms·cm
Arc resistance3.00mmASTM D495PLC 5
Compared to the anti leakage trace index3.00mmIEC 60112PLC 0
Hot wire ignition0.75mmUL 746PLC 4
3.0mmUL 746PLC 4
High arc combustion index3.0mmUL 746PLC 0
Hot wire ignition1.5mmUL 746PLC 4
thermal performanceTest ConditionTest MethodASCEND USA/R550 NAT
RTI Imp3.0mmUL 746110 °C
0.75mmUL 746110 °C
RTI Str1.5mmUL 746130 °C
Linear coefficient of thermal expansionMD：23to55°C,2.00mmISO 11359-21.2E-05 cm/cm/°C
RTI Str0.75mmUL 746130 °C
Linear coefficient of thermal expansionTD：23to55°C,2.00mmISO 11359-21E-04 cm/cm/°C
RTI Imp1.5mmUL 746110 °C
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B260 °C
RTI Elec3.0mmUL 746125 °C
1.5mmUL 746125 °C
0.75mmUL 746125 °C
RTI Str3.0mmUL 746130 °C
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A255 °C
Melting temperatureISO 11357-3260 °C
impact performanceTest ConditionTest MethodASCEND USA/R550 NAT
Impact strength of simply supported beam without notch23°CISO 179/1eU95 kJ/m²
-30°CISO 179/1eU91 kJ/m²
Supplementary InformationTest ConditionTest MethodASCEND USA/R550 NAT
Automotive Materialsthicknessd=1mmFMVSS302+

Supplier Join

Contact Us

Get App

Top

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index

+86 0755 27873515

Room 906, Global Digital Building, No. 9 Gaoxin Middle 3rd Road, Maling Community, Yuehai Subdistrict, Nanshan District, Shenzhen, Guangdong Province, China