ASA S210B UMG JAPAN
DIALAC®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | UMG JAPAN/S210B |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | ISO 2039-2 | 108 |
| Basic performance | Test Condition | Test Method | UMG JAPAN/S210B |
|---|---|---|---|
| melt mass-flow rate | 25 CM |
| Mechanical properties | Test Condition | Test Method | UMG JAPAN/S210B |
|---|---|---|---|
| bending strength | 23°C | ISO 178 | 73.0 Mpa |
| Flexural modulus | 2500 Mpa | ||
| 23°C | ISO 178 | 2500 Mpa | |
| Tensile modulus | 23°C | ISO 527-2 | 2350 Mpa |
| Charpy Notched Impact Strength | 10 KJ/m | ||
| tensile strength | 23°C | ISO 527-2 | 47.0 Mpa |
| physical property | Test Condition | Test Method | UMG JAPAN/S210B |
|---|---|---|---|
| Shrinkage rate | MD：23°C | ISO 294-4 | 0.40-0.60 % |
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 25.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | UMG JAPAN/S210B |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/Af | 83.0 °C |
| HDT | 83 °C | ||
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 8.5E-05 cm/cm/°C |