Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC GLX143-NA9C029H SABIC INNOVATIVE US
LEXAN™
Lighting applications、Plastic bag、Application in the automo
Middle flow、Thermal stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/GLX143-NA9C029H |
|---|---|---|---|
| 1.8MPa, Unannealed,64.0mm Span | ISO75-2/Af | 124 °C | |
| Linear thermal expansion coefficient | TD:23到80°C | ISO11359-2 | 7E-05 cm/cm/°C |
| Thermal Conductivity | ISO8302 | 0.20 W/m/K | |
| RTIElec | UL746 | 130 °C | |
| Ball PressureTest | 125°C | IEC60695-10-2 | Pass |
| RTI | UL746 | 125 °C | |
| Linear thermal expansion coefficient | MD:23到80°C | ISO11359-2 | 7E-05 cm/cm/°C |
| 0.45MPa, Unannealed,100mm Span | ISO75-2/Be | 136 °C | |
| Evolution Calendar intelligent importer | UL746 | 125 °C | |
| 1.8MPa, Unannealed,100mm Span | ISO75-2/Ae | 125 °C |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/GLX143-NA9C029H |
|---|---|---|---|
| Flexural Modulus | ISO178 | 2300 Mpa | |
| Tensile Stress | 断裂 | ISO527-2/50 | 70.0 Mpa |
| 屈服 | ISO527-2/50 | 65.0 Mpa | |
| Tensile Strain | 断裂 | ISO527-2/50 | 120 % |
| 屈服 | ISO527-2/50 | 6.0 % | |
| Tensile Modulus | ISO527-2/1 | 2350 Mpa | |
| Flexural Stress | ISO178 | 90.0 Mpa |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/GLX143-NA9C029H |
|---|---|---|---|
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.15 % |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 12.0 cm3/10min |
| Modeling Shrinkage | MD1 | 内部方法 | 0.50到0.70 % |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.35 % |
| Optical | Test Condition | Test Method | SABIC INNOVATIVE US/GLX143-NA9C029H |
|---|---|---|---|
| Index of Refraction | ISO489 | 1.586 | |
| Transmittance | 4000µm | ASTMD1003 | 88.0 % |
| 6000µm | ASTMD1003 | 86.0 % | |
| 5000µm | ASTMD1003 | 87.0 % | |
| 3000µm | ASTMD1003 | 89.0 % | |
| Haze | 2540µm | ASTMD1003 | <0.80 % |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/GLX143-NA9C029H |
|---|---|---|---|
| Notched Izod Impact Strength | -30°C | ISO180/1A | 12 kJ/m² |
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 无断裂 |
| Unnotched Izod Impact Strength | -30°C | ISO180/1U | 无断裂 |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 14 kJ/m² |
| 23°C | ISO179/1eA | 73 kJ/m² | |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 无断裂 |
| Unnotched Izod Impact Strength | 23°C | ISO180/1U | 无断裂 |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 70 kJ/m² |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/GLX143-NA9C029H |
|---|---|---|---|
| Glow Wire Flammability Index | 1.00mm | IEC60695-2-12 | 850 °C |
| Oxygen Index | ISO4589-2 | 25 % |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/GLX143-NA9C029H |
|---|---|---|---|
| Dielectric Strength | 1.00mm11 | IEC60243-1 | 15 KV/mm |
| 3.20mm,在油中 | IEC60243-1 | 17 KV/mm | |
| Dissipation Factor? | 60Hz | IEC60250 | 1E-03 |
| Relative Permittivity | 60Hz | IEC60250 | 2.70 |
| 1MHz | IEC60250 | 2.70 | |
| Dissipation Factor? | 50Hz | IEC60250 | 1E-03 |
| Relative Permittivity | 50Hz | IEC60250 | 2.70 |
| Dissipation Factor? | 1MHz | IEC60250 | 0.010 |