PARA Reny® 1027 Mitsubishi Chemical Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Mitsubishi Chemical Corporation/Reny® 1027 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 9.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 45 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Mitsubishi Chemical Corporation/Reny® 1027 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 18700 MPa | |
| tensile strength | 断裂 | ISO 527-2 | 227 MPa |
| Tensile strain | 断裂 | ISO 527-2 | 1.6 % |
| Flexural modulus | ISO 178 | 18300 MPa | |
| bending strength | ISO 178 | 329 MPa |
| flammability | Test Condition | Test Method | Mitsubishi Chemical Corporation/Reny® 1027 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | Mitsubishi Chemical Corporation/Reny® 1027 |
|---|---|---|---|
| Melt volume flow rate | 275°C/2.16kg | ISO 1133 | 1.10 cm³/10min |
| Shrinkage rate | 0.40 % | ||
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.80 % |
| 饱和,23°C | ISO 62 | 0.14 % | |
| density | ISO 1183 | 1.63 g/cm³ | |
| melt mass-flow rate | 275°C/2.16kg | ISO 1133 | 1.6 g/10min |
| Thermal performance | Test Condition | Test Method | Mitsubishi Chemical Corporation/Reny® 1027 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 233 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 221 °C |