density

23°C

ISO1183

g/cm³

1

Stickiness number

ISO307

cm³/g

>

ISO178

%

9

TensileCreepModule

1hr

ISO899-1

Mpa

1

Nominal tensile fracture strain

23°C

ISO527-2/50

%

>

Nominal tensile fracture strain

80°C

ISO527-2/50

%

>

Charpy Notched Impact Strength

-30°C,完全断裂

ISO179/1eA

kJ/m²

1

Charpy Notched Impact Strength

0°C,完全断裂

ISO179/1eA

kJ/m²

1

Charpy Notched Impact Strength

23°C,完全断裂

ISO179/1eA

kJ/m²

1

Tensile modulus

23°C

ISO527-2

Mpa

1

Tensile modulus

80°C

ISO527-2

Mpa

1

tensile strength

屈服,23°C

ISO527-2/50

Mpa

6

tensile strength

屈服,80°C

ISO527-2/50

Mpa

4

Tensile creep modulus

1000hr

ISO899-1

Mpa

7

Ball pressure hardness

ISO2039-1

Mpa

1

elongation

屈服,23°C

ISO527-2/50

%

8

elongation

屈服,80°C

ISO527-2/50

%

5

Bending modulus

ISO178

Mpa

1

bending strength

3.5%Strain

ISO178

Mpa

5

bending strength

--

ISO178

Mpa

9

TemperatureIndex

IEC216

°C

1

Glass transition temperature

ISO11357-2

°C

1

Hot deformation temperature

0.45MPa,未退火

ISO75-2/B

°C

1

Hot deformation temperature

1.8MPa,未退火

ISO75-2/A

°C

1

Melting temperature

DSC

°C

2

vicat softening point

--

ISO306/B

°C

1

vicat softening point

--

ISO306/A

°C

1

Linear coefficient of thermal expansion

MD：23到55°C

ISO11359-2

cm/cm/°C

9

Linear coefficient of thermal expansion

TD：23to55°C

ISO11359-2

cm/cm/°C

9

Surface resistivity

IEC60093

ohms

1

Dielectric strength

IEC60243-1

KV/mm

2

Leakage Trace Index

--6

IEC60112

V

5

Leakage Trace Index

解决方案A

IEC60112

V

6

Volume resistivity

IEC60093

ohms·cm

1

Hot filament ignition temperature

1.0mm

IEC60695-2-13

°C

7

Burning wire flammability index

1.0mm

IEC60695-2-12

°C

8