Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC ML6413 WH7D174 SABIC INNOVATIVE NANSHA
LEXAN™
Lighting applications、Electronic and Electrical、Plastic bag
High mobility、High optical masking
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/ML6413 WH7D174
Melt Volume-Flow Rate (MVR)
260°C/5.0 kg
ISO 1133
cm3/10min
2
Melt mass flow rate
260°C/5.0 kg
ASTM D1238
g/10 min
2
Shrinkage rate - flow
3.20 mm
内部方法
%
0
Water absorption rate
饱和, 23°C
ISO 62
%
0
Water absorption rate
平衡, 23°C, 50% RH
ISO 62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/ML6413 WH7D174
Tensile modulus
-- 1
ASTM D638
Mpa
2
Tensile modulus
--
ISO 527-2/1
Mpa
2
tensile strength
屈服 2
ASTM D638
Mpa
5
tensile strength
屈服
ISO 527-2/50
Mpa
6
tensile strength
断裂 2
ASTM D638
Mpa
5
tensile strength
断裂
ISO 527-2/50
Mpa
5
elongation
屈服 2
ASTM D638
%
5
elongation
屈服
ISO 527-2/50
%
5
elongation
断裂 2
ASTM D638
%
1
elongation
断裂
ISO 527-2/50
%
1
Bending modulus
50.0 mm 跨距 3
ASTM D790
Mpa
2
Bending modulus
-- 4
ISO 178
Mpa
2
bending strength
-- 4, 5
ISO 178
Mpa
9
bending strength
屈服, 50.0 mm 跨距 3
ASTM D790
Mpa
8
Dart impact equipped with measuring instruments
23°C, Total Energy
ASTM D3763
J
7
Thermal performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/ML6413 WH7D174
RTI
UL 746
°C
1
RTI Elec
UL 746
°C
1
RTI Imp
UL 746
°C
1
Hot deformation temperature
0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 7
ISO 75-2/Be
°C
1
Hot deformation temperature
1.8 MPa, 未退火, 6.40 mm
ASTM D648
°C
1
Hot deformation temperature
1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 7
ISO 75-2/Ae
°C
1
vicat softening point
--
ASTM D152512, ISO 306/B50, ISO 306/B120
°C
1
vicat softening point
--
ISO 306/B120
°C
1
Linear coefficient of thermal expansion
流动 : -40 到 40°C
ASTM E831
cm/cm/°C
7
Linear coefficient of thermal expansion
流动 : -40 到 40°C
ISO 11359-2
cm/cm/°C
7
Linear coefficient of thermal expansion
横向 : -40 到 40°C
ASTM E831
cm/cm/°C
5
Linear coefficient of thermal expansion
横向 : -40°C
ISO 11359-2
cm/cm/°C
7
Electrical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/ML6413 WH7D174
Volume resistivity
ASTM D257
ohms·cm
>
flammability
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/ML6413 WH7D174
Hot filament ignition temperature
2.0 mm
IEC 60695-2-13
°C
8
Hot filament ignition temperature
3.0 mm
IEC 60695-2-13
°C
8
Burning wire flammability index
1.6 mm
IEC 60695-2-12
°C
9