Certificates

PC LEV2200KL IDEMITSU JAPAN
TARFLON™
LCD application
UV resistance,High mobility,Aging resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
hardness | Test Condition | Test Method | IDEMITSU JAPAN/LEV2200KL |
---|---|---|---|
Rockwell hardness | M-Sale | ISO 2039-2 | 50 |
R-Sale | ISO 2039-2 | 120 |
Supplementary Information | Test Condition | Test Method | IDEMITSU JAPAN/LEV2200KL |
---|---|---|---|
ISO Shortcut | >PC< |
thermal performance | Test Condition | Test Method | IDEMITSU JAPAN/LEV2200KL |
---|---|---|---|
Hot deformation temperature | 1.8MPa,Unannealed | ISO 75-2/A | 125 °C |
Linear coefficient of thermal expansion | MD | ISO 11359-2 | 6.5E-05 cm/cm/°C |
RTI | 0.36mm | UL 746 | 130 °C |
RTI Elec | 0.36mm | UL 746 | 130 °C |
RTI Imp | 0.36mm | UL 746 | 125 °C |
mechanical properties | Test Condition | Test Method | IDEMITSU JAPAN/LEV2200KL |
---|---|---|---|
Bending modulus | ISO 178 | 2300 Mpa | |
bending strength | ISO 178 | 90.0 Mpa | |
Nominal tensile fracture strain | ISO 527-2 | 95 % | |
tensile strength | Yield | ISO 527-2 | 65.0 Mpa |
Electrical performance | Test Condition | Test Method | IDEMITSU JAPAN/LEV2200KL |
---|---|---|---|
Compared to the anti leakage trace index | CTI | UL 746 | PLC 2 |
Physical properties | Test Condition | Test Method | IDEMITSU JAPAN/LEV2200KL |
---|---|---|---|
Melt Volume Flow Rate (MVR) | 300°C/1.2kg | ISO 1133 | 12.0 cm3/10min |
Shrinkage rate | TD:1.00mm | Internal Method | 0.50-0.70 % |
MD:1.00mm | Internal Method | 0.50-0.70 % | |
Water absorption rate | Equilibrium,23°C,50%RH | ISO 62 | 0.23 % |
flammability | Test Condition | Test Method | IDEMITSU JAPAN/LEV2200KL |
---|---|---|---|
UL flame retardant rating | 0.40mm | UL 94 | V-2 |
optical performance | Test Condition | Test Method | IDEMITSU JAPAN/LEV2200KL |
---|---|---|---|
Refractive index | ASTM D542 | 1.585 | |
transmissivity | ISO 13468-1 | 90.0 % | |
turbidity | 3000μm | ASTM D1003 | 0.90 % |