Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC BFL2000 SABIC INNOVATIVE US
LEXAN™
--
Flame retardant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/BFL2000 |
|---|---|---|---|
| Surface Resistivity | ASTM D257/IEC 60093 | >1.0E+15 ohms Ω | |
| dielectric constant | ASTM D150/IEC 60250 | 3.20 | |
| Dielectric loss | ASTM D150/IEC 60250 | 0.010 | |
| arc resistance | ASTM D495/IEC 60112 | -- | |
| Volume resistivity | ASTM D257/IEC 60093 | 1.0E+15 ohm cm Ω.cm |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/BFL2000 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | -- kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 13500（13100） kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 355000（344000） kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 5.0 % | |
| Tensile modulus | ASTM D638/ISO 527 | 363000（361000） kg/cm²(MPa)[Lb/in²] | |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 1/8“5.2 kg·cm/cm(J/M)ft·lb/in | |
| elongation at break | ASTM D638/ISO 527 | 70 % | |
| Rockwell hardness | ASTM D785 | -- | |
| tensile strength | ASTM D638/ISO 527 | 8700（7250） kg/cm²(MPa)[Lb/in²] |
| other | Test Condition | Test Method | SABIC INNOVATIVE US/BFL2000 |
|---|---|---|---|
| characteristic | 加阻燃剂.无卤.无溴.阻燃 | ||
| notes | 注射成型 | ||
| Color | 本色 |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE US/BFL2000 |
|---|---|---|---|
| Fuzzy coefficient (Haze) | ISO 14782 | -- % | |
| refractive index | ASTM D542/ISO 489 | -- | |
| transmittance | ASTM D1003/ISO 13468 | -- % |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE US/BFL2000 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.50-0.70 % | |
| density | ASTM D792/ISO 1183 | 1.29 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | -- g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | 0.15 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/BFL2000 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | V-2-V-0 | |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 280 ℃（℉） |
| vicat | ASTM D1525/ISO R306 | 280 ℃（℉） | |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 0.000039 mm/mm.℃ |