TPEE DUPONT TAIWAN 7246

Injection grade

US$ 8,950 / MT

FOB Kaoshiung port, China

mechanical properties	Test Condition	Test Method	DUPONT TAIWAN/7246
Tensile creep modulus	1hr	ISO 899-1	360 Mpa
Tensile strain	Break	ISO 527-2	>300 %
Tensile modulus		ISO 527-2	550 Mpa
tensile strength	50%Strain	ISO 527-2	24.0 Mpa
Nominal tensile fracture strain		ISO 527-2	530 %
Bending modulus		ISO 178	550 Mpa
Tensile creep modulus	1000hr	ISO 899-1	310 Mpa
tensile strength	10%Strain	ISO 527-2	23.0 Mpa
Wear resistance		ISO 4649	100 mm³
tensile strength	Break	ISO 527-2	50.0 Mpa
tensile strength		5.0%Strain	ISO 527-2	14.0 Mpa
Tensile strain	Yield	ISO 527-2	26 %
tensile strength	Yield	ISO 527-2	26.0 Mpa
impact performance	Test Condition	Test Method	DUPONT TAIWAN/7246
Impact strength of cantilever beam gap	23°C	ISO 8256/1	300 kJ/m²
Charpy Notched Impact Strength	-40°C	ISO 179/1eA	7.0 kJ/m²
Charpy Notched Impact Strength		-30°C	ISO 179/1eA	8.0 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	38 kJ/m²
Impact strength of cantilever beam gap		-40°C	ISO 180/1A	7.0 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	36 kJ/m²
Physical properties	Test Condition	Test Method	DUPONT TAIWAN/7246
Water absorption rate	23°C,24hr	ISO 62	0.30 %
density		ISO 1183	1.26 g/cm³
Melt Volume Flow Rate (MVR)	240°C/2.16kg	ISO 1133	12.0 cm3/10min
Shrinkage rate	MD	ISO 294-4	1.6 %
Water absorption rate	Saturation,23°C,2.00mm	ISO 62	0.60 %
melt mass-flow rate	240°C/2.16kg	ISO 1133	13 g/10min
Shrinkage rate	TD	ISO 294-4	1.6 %
Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.20 %
flammability	Test Condition	Test Method	DUPONT TAIWAN/7246
Extreme Oxygen Index		ISO 4589-2	23 %
UL flame retardant rating	1.5mm	UL 94,IEC60695-11-10,-20	HB
Burning rate	1.00mm	ISO 3795	DNI
Electrical performance	Test Condition	Test Method	DUPONT TAIWAN/7246
Dissipation factor	100Hz	IEC 60250	0.016
Volume resistivity		IEC 60093	2E+12 ohms·cm
Dissipation factor	1MHz	IEC 60250	0.030
Relative permittivity	100Hz	IEC 60250	4.00
Surface resistivity		IEC 60093	>1.0E+15 ohms
Relative permittivity	1MHz	IEC 60250	3.50
Dielectric strength		IEC 60243-1	20 KV/mm
Compared to the anti leakage trace index		IEC 60112	PLC 0
elastomer	Test Condition	Test Method	DUPONT TAIWAN/7246
tear strength	Flow	ISO 34-1	180 kN/m
tear strength		横向Flow	ISO 34-1	170 kN/m
Filling analysis	Test Condition	Test Method	DUPONT TAIWAN/7246
SpecificHeatCapacity of Melt			2150 J/kg/°C
Melt density			1.11 g/cm³
ThermalConductivityofMelt			0.15 W/m/K
thermal performance	Test Condition	Test Method	DUPONT TAIWAN/7246
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	50.0 °C
Melting temperature		ISO 11357-3	218 °C
Vicat softening temperature	--	ISO 306/B50	140 °C
Brittle temperature		ISO 974	-97.0 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	1.8E-04 cm/cm/°C
Linear coefficient of thermal expansion		EffectiveThermalDiffusivity	ISO 11359-2	8E-08 m²/s
Vicat softening temperature	--	ISO 306/A50	205 °C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	100 °C
Glass transition temperature		ISO 11357-2	25.0 °C
Linear coefficient of thermal expansion	TD	ISO 11359-2	1.7E-04 cm/cm/°C
Supplementary Information	Test Condition	Test Method	DUPONT TAIWAN/7246
EmissionofOrganicCompounds		VDA277	300 µgC/g
hardness	Test Condition	Test Method	DUPONT TAIWAN/7246
Shore hardness	ShoreD,15Sec	ISO 868	64
Shore hardness		ShoreD	ISO 868	68