Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
LDPE LP 2427H LYONDELLBASELL SAUDI
LUPOLEN
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | LYONDELLBASELL SAUDI/LP 2427H |
|---|---|---|---|
| Akutanamide content | DIN 51454 | 0.050 % | |
| Silicon dioxide (SiO?) content | ISO 3451-1 | 0.10 % | |
| Failure energy | 50.0µm | DIN 53373 | 40.0 J/cm |
| film | Test Condition | Test Method | LYONDELLBASELL SAUDI/LP 2427H |
|---|---|---|---|
| film thickness | 20-60µm | ||
| Dart impact | 50µm,吹塑薄膜 | ASTM D1709 | 110 g |
| elongation | MD:断裂,50µm,吹塑薄膜 | ISO 527-3 | 250 % |
| film thickness | 50 µm | ||
| tensile strength | TD:50µm,吹塑薄膜 | ISO 527-3 | 21.0 Mpa |
| elongation | TD:断裂,50µm,吹塑薄膜 | ISO 527-3 | 600 % |
| tensile strength | MD:50µm,吹塑薄膜 | ISO 527-3 | 25.0 Mpa |
| Mechanical properties | Test Condition | Test Method | LYONDELLBASELL SAUDI/LP 2427H |
|---|---|---|---|
| coefficient of friction | ISO 8295 | <0.20 | |
| Tensile modulus | ISO 527-2 | 260 Mpa | |
| tensile strength | 屈服 | ISO 527-2 | 11.0 Mpa |
| optical performance | Test Condition | Test Method | LYONDELLBASELL SAUDI/LP 2427H |
|---|---|---|---|
| gloss | 20°,50.0µm,吹塑薄膜 | ASTM D2457 | >50 |
| Haze ratio | 50.0µm,吹塑薄膜 | ASTM D1003 | <9.0 % |
| gloss | 60°,50.0µm,吹塑薄膜 | ASTM D2457 | >100 |
| physical property | Test Condition | Test Method | LYONDELLBASELL SAUDI/LP 2427H |
|---|---|---|---|
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 1.9 g/10min |
| Thermal performance | Test Condition | Test Method | LYONDELLBASELL SAUDI/LP 2427H |
|---|---|---|---|
| vicat | ISO 306/A50 | 94.0 °C | |
| melting temperature | ISO 3146 | 111 °C |