Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS Sicoflex S209 Entec Polymers
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Entec Polymers/Sicoflex S209 |
|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 5.0 kJ/m² |
| 23°C | ISO 180/1A | 13 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Entec Polymers/Sicoflex S209 |
|---|---|---|---|
| tensile strength | 断裂 | ISO 527-2 | 35.0 MPa |
| Tensile strain | 断裂 | ISO 527-2 | 20 % |
| tensile strength | 屈服 | ISO 527-2 | 40.0 MPa |
| Flexural modulus | ISO 178 | 2500 MPa |
| Electrical performance | Test Condition | Test Method | Entec Polymers/Sicoflex S209 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 1 | |
| Volume resistivity | IEC 60093 | 1E+13 ohms·cm | |
| dielectric strength | 1.00mm,在油中 | IEC 60243-1 | 30 kV/mm |
| Surface Resistivity | IEC 60093 | 1E+14 ohms |
| flammability | Test Condition | Test Method | Entec Polymers/Sicoflex S209 |
|---|---|---|---|
| Hot filament ignition temperature | 1.2mm | IEC 60695-2-13 | 750 °C |
| UL flame retardant rating | 3.2mm | 内部方法 | V-0 |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | 1.6mm | 内部方法 | V-0 |
| physical property | Test Condition | Test Method | Entec Polymers/Sicoflex S209 |
|---|---|---|---|
| Shrinkage rate | ISO 2577 | 0.30to0.50 % | |
| density | ISO 1183 | 1.18 g/cm³ | |
| melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 10 g/10min |
| Thermal performance | Test Condition | Test Method | Entec Polymers/Sicoflex S209 |
|---|---|---|---|
| vicat | BallPressureTest(75°C) | Pass | |
| -- | ISO 306/A50 | 102 °C | |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 90.0 °C |
| vicat | -- | ISO 306/B50 | 93.0 °C |
Contact Us
Get App
Top