Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates

POM AW-01XAP JAPAN POLYPLASTIC
DURACON®
Household appliances、Household appliances、Electrical field、Electronic field、Automotive sector
High sliding、standard
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Supplementary Information | Test Condition | Test Method | JAPAN POLYPLASTIC/AW-01XAP |
---|---|---|---|
ColorNumber | CF2001/CD3501 |
hardness | Test Condition | Test Method | JAPAN POLYPLASTIC/AW-01XAP |
---|---|---|---|
Rockwell hardness | M级 | ISO 2039-2 | 70 |
Mechanical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/AW-01XAP |
---|---|---|---|
Wear factor | 0.98MPa,0.30m/sec4 | JISK7218 | <1.0 10^-8mm³/N·m |
0.060MPa,0.15m/sec7 | JISK7218 | 1400 10^-8mm³/N·m | |
Tensile modulus | ISO 527-2 | 2350 Mpa | |
Wear factor | 0.98MPa,0.30m/sec5 | JISK7218 | 20 10^-8mm³/N·m |
0.060MPa,0.15m/sec6 | JISK7218 | 700 10^-8mm³/N·m | |
Nominal tensile fracture strain | ISO 527-2 | 25 % | |
coefficient of friction | 与钢-动态3 | JISK7218 | 0.16 |
bending strength | ISO 178 | 75.0 Mpa | |
Flexural modulus | ISO 178 | 2200 Mpa | |
coefficient of friction | Dynamic2 | JISK7218 | 0.30 |
tensile strength | ISO 527-2 | 54.0 Mpa |
Electrical performance | Test Condition | Test Method | JAPAN POLYPLASTIC/AW-01XAP |
---|---|---|---|
Volume resistivity | IEC 60093 | 3E+14 ohms·cm | |
dielectric strength | 3.00mm | IEC 60243-1 | 20 KV/mm |
Surface Resistivity | IEC 60093 | 3E+14 ohms |
flammability | Test Condition | Test Method | JAPAN POLYPLASTIC/AW-01XAP |
---|---|---|---|
UL flame retardant rating | UL 94 | HB |
physical property | Test Condition | Test Method | JAPAN POLYPLASTIC/AW-01XAP |
---|---|---|---|
Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 8.00 cm3/10min |
Shrinkage rate | MD:2.00mm | ISO 294-4 | 2.1 % |
Water absorption rate | 23°C,24hr | ISO 62 | 0.70 % |
melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 9.0 g/10min |
Shrinkage rate | TD:2.00mm | ISO 294-4 | 1.8 % |
Thermal performance | Test Condition | Test Method | JAPAN POLYPLASTIC/AW-01XAP |
---|---|---|---|
Linear coefficient of thermal expansion | TD:23to55°C | 内部方法 | 1.3E-04 cm/cm/°C |
MD:23到55°C | 内部方法 | 1.3E-04 cm/cm/°C | |
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/A | 80.0 °C |