PA66/6 TAROMID A 260 Y0 意大利Taro Plast
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | 意大利Taro Plast/TAROMID A 260 Y0 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 2.5 kJ/m² |
| Impact strength of cantilever beam gap | -20°C,3.20mm | ASTMD256 | 25 J/m |
| 23°C,3.20mm | ASTMD256 | 40 J/m | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 50 kJ/m² |
| Mechanical properties | Test Condition | Test Method | 意大利Taro Plast/TAROMID A 260 Y0 |
|---|---|---|---|
| Flexural modulus | ASTMD790 | 3300 MPa | |
| elongation | 断裂 | ASTMD638 | 6.0 % |
| bending strength | 断裂 | ASTM D790 | 135 MPa |
| Tensile modulus | ASTMD638 | 3600 MPa | |
| tensile strength | 断裂 | ASTMD638 | 85.0 MPa |
| bending strength | -- | ISO 178 | 135 MPa |
| tensile strength | 屈服 | ASTMD638 | 95.0 MPa |
| Electrical performance | Test Condition | Test Method | 意大利Taro Plast/TAROMID A 260 Y0 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1E+15 ohms·cm | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 0 |
| flammability | Test Condition | Test Method | 意大利Taro Plast/TAROMID A 260 Y0 |
|---|---|---|---|
| UL flame retardant rating | 0.55mm | UL 94 | V-0 |
| Burning wire flammability index | 1.2mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 1.2mm | IEC 60695-2-13 | 775 °C |
| UL flame retardant rating | 3.2mm | UL 94 | V-0 |
| 1.6mm | UL 94 | V-0 | |
| Limiting Oxygen Index | ASTM D2863 | 32 % |
| physical property | Test Condition | Test Method | 意大利Taro Plast/TAROMID A 260 Y0 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 1.0to1.5 % |
| Water absorption rate | 饱和 | ASTM D570 | 8.0 % |
| density | ASTMD792 | 1.16to1.18 g/cm³ | |
| Water absorption rate | 23°C,24hr | ASTMD570 | 1.0to1.5 % |
| 饱和,23°C | ISO 62 | 8.0 % | |
| Shrinkage rate | TD | ASTM D955 | 1.5to2.5 % |
| Thermal performance | Test Condition | Test Method | 意大利Taro Plast/TAROMID A 260 Y0 |
|---|---|---|---|
| Hot deformation temperature (HDT) | 0.45MPa,未退火，HDT | ASTMD648 | 225 °C |
| 1.8MPa,未退火，HDT | ASTMD648 | 90.0 °C | |
| Continuous use temperature | --5 | IEC 60216 | 120 °C |
| --4 | IEC 60216 | 80.0 °C | |
| vicat | -- | ASTMD15257 | 236 °C |
| melting temperature | ASTMD211 | 250to256 °C | |
| vicat | -- | ASTMD15256 | 248 °C |
| MD：-30到30°C | ASTM D696 | 8E-05 cm/cm/°C |