PEI EX00548C SABIC INNOVATIVE US
ULTEM™
Plastic bag
Thermal stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/EX00548C |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 33 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 4.7 kJ/m² |
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 4.90 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/EX00548C |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 3200 Mpa | |
| elongation | 屈服 | ASTM D638 | 6.1 % |
| bending strength | ASTM D790 | 149 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 6.0 % |
| tensile strength | 断裂 | ASTM D638 | 83.7 Mpa |
| 断裂 | ISO 527-2 | 85.0 Mpa | |
| Flexural modulus | ASTM D790 | 3450 Mpa | |
| Tensile modulus | ASTM D638 | 3030 Mpa | |
| elongation | 断裂 | ASTM D638 | 8.1 % |
| bending strength | ISO 178 | 143 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 7.6 % |
| Flexural modulus | ISO 178 | 3390 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 85.4 Mpa |
| 屈服 | ISO 527-2 | 86.0 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/EX00548C |
|---|---|---|---|
| Shrinkage rate | MD:24小时 | ISO 294-4 | 0.66 % |
| MD：24小时 | ASTM D955 | 0.70 % | |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.22 % |
| Shrinkage rate | TD：24hr | ASTM D955 | 0.70 % |
| TD:24小时 | ISO 294-4 | 0.70 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/EX00548C |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,64.0mm跨距，HDT | ISO 75-2/Af | 184 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 185 °C |