PBT+PET POCAN® ECO T 3230 000000 LANXESS GERMANY
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LANXESS GERMANY/POCAN® ECO T 3230 000000 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 55 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | <10 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 55 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | <10 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | <10 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 65 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | <10 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 55 kJ/m² |
| Supplementary Information | Test Condition | Test Method | LANXESS GERMANY/POCAN® ECO T 3230 000000 |
|---|---|---|---|
| ISO Shortcut | ISO 7792 | PBT+PET.GHMR.09-100.GF30 |
| Mechanical properties | Test Condition | Test Method | LANXESS GERMANY/POCAN® ECO T 3230 000000 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 2.8 % |
| tensile strength | 断裂,23°C | ISO 527-2/5 | 145 MPa |
| Bending Strain | 23°C | 3.0 % | |
| Tensile modulus | 23°C | ISO 527-2/1 | 10400 MPa |
| Flexural modulus | 23°C | ISO 178/A | 10300 MPa |
| bending strength | 23°C | ISO 178 | 230 MPa |
| Electrical performance | Test Condition | Test Method | LANXESS GERMANY/POCAN® ECO T 3230 000000 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 2 |
| physical property | Test Condition | Test Method | LANXESS GERMANY/POCAN® ECO T 3230 000000 |
|---|---|---|---|
| Shrinkage rate | TD:120°C,2hr,2.00mm3 | ISO 294-4 | 0.20 % |
| MD:270°C,2.00mm2 | ISO 294-4 | 0.30 % | |
| density | 23°C | ISO 1183 | 1.55 g/cm³ |
| Apparent density | ISO 60 | 0.80 g/cm³ | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.10 % |
| 饱和,23°C | ISO 62 | 0.30 % | |
| Shrinkage rate | TD:270°C,2.00mm2 | ISO 294-4 | 0.90 % |
| Melt volume flow rate | 260°C/5.0kg | ISO 1133 | 30.0 cm³/10min |
| Shrinkage rate | MD:120°C,2hr,2.00mm3 | ISO 294-4 | 0.10 % |
| Thermal performance | Test Condition | Test Method | LANXESS GERMANY/POCAN® ECO T 3230 000000 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 225to250 °C | |
| vicat | ISO 306/B120 | 205 °C | |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 3E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 220 °C |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO 11359-2 | 9E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 200 °C |