PPO GN3101F KA02 LG GUANGZHOU
LUMILOY®
Home appliance components、Electrical applications
Thermal stability、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | LG GUANGZHOU/GN3101F KA02 |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/5 | 48.0 Mpa |
| bending strength | ISO 178 | 89.0 Mpa | |
| Flexural modulus | ISO 178 | 3670 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 52 % |
| flammability | Test Condition | Test Method | LG GUANGZHOU/GN3101F KA02 |
|---|---|---|---|
| UL flame retardant rating | 3.0 mm | UL 94 | V-0 |
| 0.75 mm | UL 94 | V-0 | |
| 1.5 mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | LG GUANGZHOU/GN3101F KA02 |
|---|---|---|---|
| melt mass-flow rate | 260°C/5.0 kg | ISO 1133 | 11 g/10 min |
| 250°C/2.16 kg | ISO 1133 | 1.8 g/10 min |
| Thermal performance | Test Condition | Test Method | LG GUANGZHOU/GN3101F KA02 |
|---|---|---|---|
| vicat | ISO 306/B50 | 109 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火, 4.00 mm，HDT | ISO 75-2/A | 94.0 °C |
| RTI Imp | UL 746 | 80.0 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火, 4.00 mm，HDT | ISO 75-2/B | 104 °C |
| RTI | UL 746 | 80.0 °C | |
| RTI Elec | UL 746 | 80.0 °C |
| injection | Test Condition | Test Method | LG GUANGZHOU/GN3101F KA02 |
|---|---|---|---|
| drying time | 3.0 to 4.0 hr | ||
| screw speed | < 80 rpm | ||
| Suggested maximum moisture content | 0.020 % | ||
| Temperature in the middle of the barrel | 270 to 290 °C | ||
| Temperature at the rear of the barrel | 260 to 270 °C | ||
| Processing (melt) temperature | 260 to 300 °C | ||
| drying temperature | 80 to 100 °C | ||
| Temperature at the front of the material cylinder | 290 to 300 °C | ||
| Back pressure | 0.981 to 3.92 Mpa | ||
| Temperature | 60 to 80 °C | ||
| Spray nozzle temperature | 270 to 290 °C |