Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PET 130 BK112 BASF USA
Petra®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | BASF USA/130 BK112 |
|---|---|---|---|
| Rockwell hardness | R 级 | ASTM D785 | 118 |
| Mechanical properties | Test Condition | Test Method | BASF USA/130 BK112 |
|---|---|---|---|
| tensile strength | 断裂, 120°C | ISO 527-2 | 54.0 Mpa |
| 断裂, 150°C | ISO 527-2 | 42.0 Mpa | |
| elongation | 断裂, 150°C | ISO 527-2 | 4.0 % |
| tensile strength | 断裂, 23°C | ASTM D638, ISO 527-2 | 145 Mpa |
| elongation | 断裂, 23°C | ASTM D638, ISO 527-2 | 3.0 % |
| Flexural modulus | 23°C | ISO 178 | 8250 Mpa |
| bending strength | 23°C | ASTM D790 | 230 Mpa |
| elongation | 断裂, -40°C | ISO 527-2 | 2.3 % |
| Tensile modulus | 23°C | ISO 527-2 | 10200 Mpa |
| elongation | 断裂, 120°C | ISO 527-2 | 4.0 % |
| tensile strength | 断裂, -40°C | ISO 527-2 | 211 Mpa |
| Flexural modulus | 23°C | ASTM D790 | 8760 Mpa |
| Electrical performance | Test Condition | Test Method | BASF USA/130 BK112 |
|---|---|---|---|
| Volume resistivity | -- | IEC 60093 | > 1.0E+13 ohms·cm |
| 1.50 mm | ASTM D257 | > 1.0E+13 ohms·cm |
| flammability | Test Condition | Test Method | BASF USA/130 BK112 |
|---|---|---|---|
| UL flame retardant rating | 3.0 mm | UL 94 | HB |
| 0.75 mm | UL 94 | HB | |
| 1.5 mm | UL 94 | HB |
| physical property | Test Condition | Test Method | BASF USA/130 BK112 |
|---|---|---|---|
| Shrinkage rate - flow | 3.18 mm | 0.40 % |
| Thermal performance | Test Condition | Test Method | BASF USA/130 BK112 |
|---|---|---|---|
| Thermal deformation temperature under load | 0.45 MPa, 未退火 | ASTM D648 | 235 °C |
| 1.8 MPa, 未退火 | ASTM D648 | 215 °C | |
| ASTM D3418, ISO 3146 | 245 °C | ||
| ASTM E831 | 2.3E-5 cm/cm/°C | ||
| RTI Elec | 0.75 mm | UL 746 | 140 °C |
| Thermal deformation temperature under load | 1.8 MPa, 未退火 | ISO 75-2/A | 210 °C |
| RTI | 0.75 mm | UL 746 | 140 °C |
| RTI Imp | 3.0 mm | UL 746 | 140 °C |
| RTI Elec | 1.5 mm | UL 746 | 140 °C |
| RTI Imp | 0.75 mm | UL 746 | 140 °C |
| RTI | 3.0 mm | UL 746 | 140 °C |
| RTI Elec | 3.0 mm | UL 746 | 140 °C |
| Thermal deformation temperature under load | 0.45 MPa, 未退火 | ISO 75-2/B | 240 °C |
| RTI Imp | 1.5 mm | UL 746 | 140 °C |
| RTI | 1.5 mm | UL 746 | 140 °C |
| injection | Test Condition | Test Method | BASF USA/130 BK112 |
|---|---|---|---|
| Temperature | 100 到 110 °C | ||
| Processing (melt) temperature | 280 到 300 °C | ||
| drying temperature | 120 °C | ||
| Injection Pressure | 3.50 到 12.5 Mpa | ||
| injection speed | 快速 | ||
| drying time | 2.0 到 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % |