| Impact resistance | Test Condition | Test Method | VICTREX UK/90G |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 4.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | NoBreak |
| Suspended wall beam without notch impact strength | 23°C | ISO 180 | NoBreak |
| Impact strength of cantilever beam gap | 23°C | ISO 180/A | 4.5 kJ/m² |
| hardness | Test Condition | Test Method | VICTREX UK/90G |
|---|---|---|---|
| Shore hardness | 邵氏D,23°C | ISO 868 | 85 |
| Mechanical properties | Test Condition | Test Method | VICTREX UK/90G |
|---|---|---|---|
| bending strength | 23°C8 | ISO 178 | 175 Mpa |
| 3.5%Strain,23°C | ISO 178 | 130 Mpa | |
| 275°C | ISO 178 | 13.5 Mpa | |
| Tensile strain | 断裂,23°C | ISO 527-2 | 20 % |
| bending strength | 125°C | ISO 178 | 90.0 Mpa |
| compression stress | 120°C | ISO 604 | 80.0 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2 | 105 Mpa |
| Flexural modulus | 23°C | ISO 178 | 3900 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 4100 Mpa |
| compression stress | 23°C | ISO 604 | 130 Mpa |
| bending strength | 175°C | ISO 178 | 20.0 Mpa |
| Electrical performance | Test Condition | Test Method | VICTREX UK/90G |
|---|---|---|---|
| dielectric constant | 23°C,1kHz | IEC 60250 | 3.10 |
| Volume resistivity | 125°C | IEC 60093 | 1E+15 ohms·cm |
| 23°C | IEC 60093 | 1E+16 ohms·cm | |
| dielectric strength | 2.50mm | IEC 60243-1 | 23 KV/mm |
| Dissipation Factor | 23°C,1MHz | IEC 60250 | 4E-03 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V | |
| Volume resistivity | 275°C | IEC 60093 | 1E+09 ohms·cm |
| flammability | Test Condition | Test Method | VICTREX UK/90G |
|---|---|---|---|
| toxicity | COcontent | NES713 | 0.0740 |
| CO2content | NES713 | 0.150 | |
| Totalgases | NES713 | 0.220 | |
| Limiting Oxygen Index | --14 | ISO 4589-2 | 35 % |
| --13 | ISO 4589-2 | 24 % | |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 960 °C |
| physical property | Test Condition | Test Method | VICTREX UK/90G |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 1.3 % |
| spiral flow length | --5 | 内部方法 | 28.0 CM |
| Shrinkage rate | MD | ISO 294-4 | 1.0 % |
| spiral flow length | --4 | 内部方法 | 24.5 CM |
| --6 | 内部方法 | 33.0 CM | |
| density | 比重 | ISO 1183 | 1.30 g/cm³ |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.45 % |
| 100°C，饱和 | ISO 62 | 0.55 % | |
| MeltViscosity | 400°C | ISO 11443 | 90.0 Pa·s |
| Thermal performance | Test Condition | Test Method | VICTREX UK/90G |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/Af | 156 °C |
| 1.8MPa,Annealed，HDT | ISO 75-2/Af | 167 °C | |
| melting temperature | ISO 11357-3 | 343 °C | |
| Glass transition temperature (Tg) | ISO 11357 | 143 °C | |
| Linear coefficient of thermal expansion | MD：<143°C | ISO 11359-2 | 5E-05 cm/cm/°C |
| thermal conductivity | 23°C11 | ISO 22007-4 | 0.29 W/m/K |
| 23°C12 | ISO 22007-4 | 0.32 W/m/K | |
| Linear coefficient of thermal expansion | TD：>143°C | ISO 11359-2 | 1.4E-04 cm/cm/°C |
| TD：<143°C | ISO 11359-2 | 5.5E-05 cm/cm/°C | |
| MD：>143°C | ISO 11359-2 | 1.2E-04 cm/cm/°C |