Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT SK602 WT DUPONT USA
Cristin®
Electronic and electrical、Automotive Applications
Flame retardant、Glass fiber reinforced、Filler: Glass fiber reinf、15% filler by weight、15% filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/SK602 WT |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 7.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 40 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 5.0 kJ/m² |
| Supplementary Information | Test Condition | Test Method | DUPONT USA/SK602 WT |
|---|---|---|---|
| Odor | VDA270 | 3.00 | |
| Emissions of Organic Compounds | VDA277 | 140 µgC/g |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/SK602 WT |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 5800 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 3.5 % |
| Tensile modulus | 0.00 mm, 23 ℃, Injection Molded | ISO 527-1 | 5700 MPa |
| tensile strength | 断裂 | ISO 527-2 | 109 Mpa |
| Electrical performance | Test Condition | Test Method | DUPONT USA/SK602 WT |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
| dielectric strength | IEC 60243-1 | 35 KV/mm | |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| Dissipation Factor | 100Hz | IEC 60250 | 7E-04 |
| relative permittivity | 100Hz | IEC 60250 | 3.70 |
| 1MHz | IEC 60250 | 3.60 | |
| Surface Resistivity | IEC 60093 | 1E+14 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.017 |
| flammability | Test Condition | Test Method | DUPONT USA/SK602 WT |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | IEC 60695-11-10,-20 | HB |
| 3.0mm | UL 94 | HB | |
| Fogging-G-value | condensate | ISO 6452 | 1E-04 g |
| UL flame retardant rating | 1.5mm | IEC 60695-11-10,-20 | HB |
| FMVSS flammability | FMVSS302 | B | |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| burning rate | 1.00mm | ISO 3795 | 30 mm/min |
| physical property | Test Condition | Test Method | DUPONT USA/SK602 WT |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 1.1 % |
| MD | ISO 294-4 | 0.40 % | |
| Ejection Temperature | 170 °C | ||
| density | ISO 1183 | 1.41 g/cm³ | |
| Shrinkage rate | MDLength2(2.00mm) | ISO 294-4 | 360 mm |
| Thermal performance | Test Condition | Test Method | DUPONT USA/SK602 WT |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 225 °C | |
| UL flame retardant rating | 3.00 mm | UL 94 | HB |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 200 °C |
| UL flame retardant rating | 1.50 mm | UL 94 | HB |
| 6.00 mm | UL 94 | HB |