PBT 1494X02 PBT vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Reference Price

PBT TORAY JAPAN 1494X02

Flame retardant grade

US$ 3,350 / MT

FOB Guangzhou port, China

Electrical performance	Test Condition	Test Method	TORAY JAPAN/1494X02
Dissipation factor	23°C	IEC 60250	0.020 1MHz
Dielectric constant	23°C	IEC 60250	3.40 1MHz
Dielectric strength	短时·23℃·1/8时	ASTM D-149	17 KV/mm
Volume resistivity		ASTM D-257	1.0 cm×10
Arc resistance		ASTM D-495	70 秒
Volume resistivity		IEC 60093	2E+16 Ω.cm
Dielectric strength		IEC 60243-1	26 KV/mm
Dielectric constant		ASTM D150/IEC 60250	3.4
Dissipation factor	耐电弧性	IEC 61621	70.0 S
Volume resistivity		ASTM D257/IEC 60093	1.0x10^14 Ω.cm
Physical properties	Test Condition	Test Method	TORAY JAPAN/1494X02
Friction coefficient	本身	ASTM D-1894	0.18
Shrinkage rate	MD	ISO 294-4	1.5 %
Hot deformation temperature	18.6kg/cm	ASTM D-648	60 °C
Water absorption rate	(23°C,24hr)	ISO 62	0.080 %
Shrinkage rate	TD	ISO 294-4	2.0 %
density		ASTM D792/ISO 1183	1.43
Water absorption rate		ASTM D570/ISO 62	0.08 %
Taber abraser	1.000g·CS-17轮	ASTM D-1044	13 毫克/1.000m
Friction coefficient	金属	ASTM D-1894	0.14
Hot deformation temperature	4.6kg/cm	ASTM D-648	165 °C
Shrinkage rate	80×80×3板材		1.5-2.0 %
other	Test Condition	Test Method	TORAY JAPAN/1494X02
characteristic			非增强阻燃等级.V-0
mechanical properties	Test Condition	Test Method	TORAY JAPAN/1494X02
Impact strength of cantilever beam gap	Unnotched，-40℃	ASTM D-256	50 kg·cm/cm
Impact strength of cantilever beam gap		Notched，23℃	ASTM D-256	3.5 kg·cm/cm
tensile strength	23°C	ISO 527-2	64.0 Mpa
bending strength	23°C	ISO 178	105 Mpa
Impact strength of cantilever beam gap	Notched，-40℃	ASTM D-256	3.0 kg·cm/cm
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	66 kJ/m²
bending strength		ASTM D790/ISO 178	95 kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D-785	119
Impact strength of cantilever beam gap		ASTM D256/ISO 179	90 kg·cm/cm(J/M)ft·lb/in
Rockwell hardness		ASTM D785	M86
Bending modulus	23℃	ASTM D-790	28 kg/cm
Bending modulus			ASTM D790/ISO 178	2800 kg/cm²(MPa)[Lb/in²]
Tensile modulus	23°C	ISO 527-2	3000 Mpa
compressive strength	23℃	ASTM D-695	930 kg/cm
tensile strength	23℃	ASTM D-638	620 kg/cm
Impact strength of cantilever beam gap	Unnotched，23℃	ASTM D-256	120 kg·cm/cm
Elongation at Break	23°C	ISO 527-2	8.0 %
bending strength	23℃	ASTM D-790	940 kg/cm
Elongation at Break		ASTM D638/ISO 527	20 %
Elongation at Break		23℃	ASTM D-638	20 %
Bending modulus	23°C	ISO 178	2900 Mpa
tensile strength		ASTM D638/ISO 527	65 kg/cm²(MPa)[Lb/in²]
Charpy Notched Impact Strength	23°C	ISO 179/1eA	2.5 kJ/m²
thermal performance	Test Condition	Test Method	TORAY JAPAN/1494X02
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	9.0x10^-5 mm/mm.℃
Hot deformation temperature	0.45MPaUnannealed	ISO 75-2/Bf	136 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	9E-05 cm/cm/°C
Linear coefficient of thermal expansion			ASTM D-696	9.0 cm/cm℃×10
Hot deformation temperature	1.80MPaAnnealed	ISO 75-2/Af	64.0 °C
Combustibility (rate)		UL 94	V-0
Basic Performance	Test Condition	Test Method	TORAY JAPAN/1494X02
Water absorption rate	23℃·24hr	ASTM D-570	0.08 %
hardness	Test Condition	Test Method	TORAY JAPAN/1494X02
Rockwell hardness		ISO 2039-2	82 M（Scale）
flammability	Test Condition	Test Method	TORAY JAPAN/1494X02
UL flame retardant rating		UL -94	V-0 3.00mm